Stresses and Deformations Arised from Uniform Inherent Strains in Thin-Walled Pipes
スポンサーリンク
概要
- 論文の詳細を見る
- 社団法人溶接学会の論文
- 1983-04-01
著者
-
Satoh Kunihiko
Department Of Welding Engineering Osaka University
-
Toyoda Msaao
Osaka University
-
TOYODA Masao
Osaka University
-
Suita Yoshikazu
Department Of Mechanical Engineering Takamatsu National College Of Technology
-
Suita Yoshikazu
Takamatsu National College Of Technology
-
Tanaka Masahumi
Department Of Mechanical Engineering Takamatsu National College Of Technology
-
Tanaka Masabumi
Department Of Mechanical Engineering Takamatsu National College Of Technology
関連論文
- Formation of Trimethylpentanes from Isobutane and 1 - Butene Catalyzed by Sulfated Metal Oxides
- Effect of Mechanical Heterogeneity on Fracture Toughness Evaluation of Steel Welds
- Notch Toughness Evaluation of HT80 Electron Beam Weld Metal by Charpy Test
- 125 EMPIRIC STUDY TO RELATE THE RRC- AND TRC-TESTS WITH THE IMPLANT TEST ON MECHANICAL BASIS
- Static Tensile and Brittle Fracture Strengths of Soft Welded Joints
- Effect of Residual Stress and Mechanical Heterogeneity on Brittle Fracture Strength of Welded Joints
- Controlling Parameters of Residual Stresses and Deformations in Welded Thin Cylindrical Shells
- Residual Stresses and Deformations in Thin Cylindrical Shells due to Longitudinal Welds
- Residual Stresses and Deformations in Thin Cylindrical Shells due to Circumferential Welds
- Effect of Welding Conditions on Residual Stress Distributions in Basic Welded Joints
- Experimental Investigation on Applicability of Stress Field Parameter F_I for Weld Hydrogen Cracking
- Mechanical Controlling Factor of Weld Hydrogen Cracking
- Probabilistic Analysis of Fracture Toughness of Weld HAZ with LBZ
- A Probabilistic Approach to Evaluation of Fracture Toughness of Welds with Heterogeneity
- Study on Reasonable Inspection Method for Welds Considering Detectability of NDT
- Controlling Parameters of Residual Stresses and Deformations in Welded Thin Cylindrical Shells
- Stresses and Deformations Arised from Uniform Inherent Strains in Thin-Walled Pipes
- 10. Preheat Temperature for Preventing Root Cracking in Continuous Multi Pass Welding
- Fracture Toughness Evaluation of Welds with Mechanical Heterogeneity
- Analysis of Residual Stresses in Evaporated and Plating Films
- Effect of Strength Mis-Match on Fracture Mechanical Behavior of HAZ-Notched Weld Joint