Relationship between A_f Temperature and Load Changes in Ni-Ti Orthodontic Wire under Different Thermomechanical Conditions
スポンサーリンク
概要
- 論文の詳細を見る
Simple three point bending tests were performed on Ni-Ti wires with three different A_f points (1℃, 13℃ and 34℃) to clarify the relationship between A_f temperature and load changes under constant deformation. Each wire was deformed at 37℃ and then thermal changes were imposed by temperatures of 2℃ or 60℃. The load changes with thermal changes from 37℃ to 2℃ or 60℃ showed the same tendency on the wires with different A_f points: In the loading stage, the load became lower than the initial level at 37℃ and in the unloading stage, the load became higher than the initial load. The largest load change in the unloading stage was measured with the l3℃ A_f point wire. Care must be taken when handling Ni-Ti wire with an A_f point of less than 1℃ in order to prevent it from reaching the limit of critical stress of slip deformation when the temperature in the mouth rises to above 40℃.
- 日本歯科理工学会の論文
著者
-
KAWASHIMA Isao
Department of Dental Materials Science, School of Dentistry, Health Sciences University of Hokkaido,
-
OHNO Hiroki
Department of Dental Materials Science, School of Dentistry, Health Sciences University of Hokkaido,
-
Ohno Hiroki
Department Of Biology Kyoto University Of Education
-
Ohno Hiroki
Department Of Dental Materials Science School Of Dentistry Health Sciences University Of Hokkaido
-
Kawashima Isao
Department Of Dental Materials Science Health Sciences University Of Hokkaido School Of Dentistry
-
SACHDEVA Rohit
Department of Orthodontics, Baylor College of Dentistry-Taxas A&M University System
-
Kawashima I
Department Of Dental Materials Science School Of Dentistry Health Sciences University Of Hokkaido
-
Sachdeva Rohit
Department Of Orthodontics Baylor College Of Dentistry-taxas A&m University System
関連論文
- X-ray scanning analytical microscopic and scanning electron microscopic studies of an unusual case of dens invaginatus
- Hydroxyapatite Film Coating by Thermally Induced Liquid-phase Deposition Method for Titanium Implants
- Mechanism by which Porous Structure is Formed on the Surface of Gold Alloy Containing Only Cu as Base Metal
- XPS Study on the Weakest Zone in the Adhesion Structure between Resin Containing 4-META and Precious Metal Alloys Treated with Different Surface Modification Methods
- Adhesion of Adhesive Resin to Dental Precious Metal Alloys : Part II The Relationship between Surface Structure of Au-In Alloys and Adhesive Ability with 4-META Resin
- Mechanism of Adhesion between 4-META Resin and Alloys Based on Bolger's Acid-base Interaction
- Adhesion of Adhesive Resin to Dental Precious Metal Alloys : Part I New Precious Metal Alloys with Base Metals for Resin Bonding
- アークイオンプレーティング法によりNi-50Ti合金上に創成したTiN膜の表面性状と耐食性
- In Vitro Corrosion of Dental Ag-based Alloys in Polyvinylpyrrolidone Iodine Solution
- In Vitro Corrosion Characteristics of Commercially Available Orthodontic Wires
- Corrosion Characteristics of Ferric and Austenitic Stainless Steels for Dental Magnetic Attachment
- Corrosion Resistance and Biocompatibility of High Nitrogen-bearing Stainless Steels
- Effect of Cr and Cu Addition on Corrosion Behavior of Ni-Ti Alloys
- Relationship between A_f Temperature and Load Changes in Ni-Ti Orthodontic Wire under Different Thermomechanical Conditions
- Gold Alloys for Resin Bonding including Small Amount Base Metals : Structural Changes of Alloy Surface by the High-temperature Oxidation
- Rate of Parasitism of the Antlion Larvae, Myrmeleon bore (Neuroptera : Myrmeleontidae) by the Bee Fly, Villa myrmeleonostena (Diptera : Bombyliidae)
- In vivo Corrosion and Tarnish of Dental Au-based and Ag-based Alloy Restorations
- Multilevel Storage in N-Doped Sb2Te3-Based Lateral Phase Change Memory with an Additional Top TiN Layer
- Effect of mold temperature on the microstructure and corrosion properties of a 14-karat gold alloy