bcc-FeCoNi/bcc-like-CrMnPt膜の交換結合特性とCrMnPt膜の格子歪
スポンサーリンク
概要
- 論文の詳細を見る
Exchange coupling of bcc-Fe_<55>Co_<30>Ni_<15>/bcc-like-Cr_<45>Mn_<45>Pt_<10> films and lattice distortion of their CrMnPt films were investigated. In this system, the unidirectional anisotropy constant(K_e)continued to increase even if the CrMnPt thickness(t_<CrMnPt>)was more than the critical thickness, because the lattice distortion of the CrMnPt film was amplified by increasing t_<CrMnPt>. The reason for this was that the total stress applied to the lattice of the CrMnPt film through annealing, due to a positive spontaneous lattice distortion of the CrMnPt film and a negative FeCoNi/CrMnPt lattice mismatch, increased with the depth in the CrMnPt layer from the interface. The K_e did not saturate at the critical thickness because of the negative FeCoNi/CrMnPt lattice mismatch.
- 社団法人日本磁気学会の論文
- 1998-09-01
著者
関連論文
- 熱処理によるFePt合金薄膜の微細構造の変化と規則化(信号処理及び一般)
- CrMnPt反強磁性膜を用いたFe_3O_4膜への交換磁気異方性の付与
- スピンバルブヘッド用CrMnPt反強磁性膜の開発
- Fe-Fe_3O_4強磁性膜を用いたスピンバルブ膜の検討
- ZnO下地膜を用いた高結晶配向性スピンバルブ膜の検討 : 磁気抵抗効果・交換結合
- Fe_3O_4膜の極薄膜化における磁気・電気特性の変化
- ハーフメタル薄膜の磁気、伝導特性
- Au膜上のハーフメタルFe_3O_4薄膜の開発とその応用
- ハーフメタルFe_3O_4膜の開発と応用 : ハーフメタル適用GMR
- 熱処理によるFePt合金薄膜の微細構造の変化と規則化 (マルチメディアストレージ)
- CrMn系反強磁性膜とNiFe膜の交換結合
- CrMn系反強磁性膜とNiFe膜の交換結合
- ZnO下地膜を用いた高結晶配向性スピンバルブ膜の検討
- CrMnPt反強磁性膜の応力誘導磁気異方性
- NiO/α-Fe_2O_3/CoO反強磁性膜とNiFe膜との交換結合
- bcc-FeCoNi/bcc-like-CrMnPt膜の交換結合特性とCrMnPt膜の格子歪
- 8aWA-6 Fe_3O_4を用いたGMR膜の磁気抵抗効果と電気伝導(トンネル磁気抵抗・メゾスコピック伝導,領域3)