211 SP 処理球状黒鉛鋳鉄のき裂特性と破面観察に関する研究

概要

論文の詳細を見る
Rotating bending fatigue tests were carried out on specimens of ferrite-pearlitic cast irons and pearlitic ductile cast irons with a shot-peening (SP) treatment. It has been reported that sites of the fatigue crack initiation are transferred from the surface to subsurface in the range of longer life region over (10)^7 cycles. So the initiation and the propagation behaviors of the surface fatigue cracks with the compressive residual induced by the SP treatment and also the subsurface fatigue crack were investigated by the detailed observations of the specimen surface and the fracture surface. As a result, the non-propagating surface cracks under the influence of the SP treatments were observed. And the flat area of subsurface fatigue cracks similar to the fish-eye region increased with decreasing of the stress amplitude.
一般社団法人日本機械学会の論文
2000-10-05