腐食ピット成長に基づく腐食疲労き裂発生余寿命予測
スポンサーリンク
概要
- 論文の詳細を見る
Corrosion fatigue crack initiation behavior of low alloy steel has been investigated in water. It was observed that corrosion fatigue process was composed of three stages, namely, corrosion pit growth, transition into crack from the corrosion pit and corrosion fatigue crack propagation. The corrosion pit size was found to increase with time t following the relation : corrosion pit size ∝ t^<1/3>. The condition of transition into crack from the corrosion pit was determined by a stress intensity factor, by assuming the corrosion pit as a sharp crack. The critical pit condition (ΔK)_p was 1.2 MPa √<m> for 2.5 NiCrMoV and 3.5 NiCrMoV in 90℃ water with 100 ppb dissolved oxygen. Based on the abovementioned results, residual life prediction method for corrosion fatigue crack initiation was proposed.
- 一般社団法人日本機械学会の論文
- 1987-11-25
著者
関連論文
- 低合金鋼の変動ひずみ下の環境助長割れ : (第3報, 腐食電流に基づくき裂発生寿命評価モデル)
- 低合金鋼の変動ひずみ下の環境助長割れ : 第2報, 腐食電流計測によるき裂発生加速メカニズムの検討
- 低合金鋼の変動ひずみ下の環境助長割れ : 第1報, き裂発生・伝ぱの加速に影響するひずみ波形因子
- 3次元破面解析技術FRASTA法の適用性に関する研究
- 疲労破面粗さに基づく作用応力推定
- ミニコンピュータの利用による疲労試験における計測の高精度自動化
- ランダムを含む定常変動荷重下の疲労き裂開閉口挙動とき裂進展速度の推定法 : 第2報,高進展速度領域への拡張
- ランダムを含む定常変動荷重下のき裂開閉口挙動とき裂進展速度の推定法 : 第1報,平均荷重の影響ならびに波形カウント法の検討
- 低K領域における変動荷重下の疲労き裂進展挙動と進展速度の評価法
- 疲労き裂進展下限界条件試験法に対する検討 : き裂開閉口挙動に及ぼす荷重履歴の影響
- 126 き裂開閉口挙動の測定による疲労き裂進展下限界条件試験法に対する検討
- 平面ひずみ条件下の疲労き裂進展とき裂開閉口挙動
- 低K領域における2段ならびに3段多重変動荷重下の疲労き裂進展と開閉口挙動
- K_ レベルをはさむ繰返し2段変動荷重下の疲労き裂進展
- フレッティング疲労ミクロき裂発生に対する限界相対すべり量について
- 接触端部応力に着目したフレッティング疲労き裂発生条件の検討
- 17-4PHステンレス鋼の腐食疲労き裂発生メカニズムに関する一検討
- き裂先端特異応力分布を利用したき裂長さの自動計測
- 衝撃破壊に及ぼす予負荷の効果について
- 12CrMo鋼のSCC・疲労相互作用下のき裂伝ぱに及ぼす焼戻し温度の影響
- SCC・疲労相互作用下の破面形態とき裂伝ぱ速度について
- 低サイクル腐食疲労に及ぼす応力保持効果の電気化学的検討
- ΔK_試験機の開発および迅速ΔK_試験法の検討
- 腐食ピット成長に着目した12CrMo鋼の腐食疲労き裂発生条件の定量評価
- 腐食ピット成長に基づく腐食疲労き裂発生余寿命予測
- 構造物に発生したき裂のK値測定用ゲージの開発
- K値ゲージと構造物中き裂の監視装置