破断延性と低サイクル疲労寿命の関連について

概要

論文の詳細を見る
A low cycle fatigue test and a micro-crack propagation test were carried out under push-pull loading on low carbon steel and on pure iron, with special interest in the relation between the fracture ductility and the low cycle fatigue life. Results show that the low cycle fatigue life is not sensitive to the change in fracture ductility of the material for the ordinary low cycle regime in which the development of small surface cracks leads to the fracture of the specimen, and that this is closely related to the evidence showing that the rate of microcrack extension is not appreciably affected by the fracture ductility of the materials. Calculation of low cycle fatigue life on the basis of the law of small crack growth proposed in recent years revealed that only a small difference in fatigue life appears in the high and low ductility materials.
一般社団法人日本機械学会の論文
1987-12-25