トポグラフィ破面解析による高強度鋼の内部疲労き裂発生・進展機構に関する研究(<特集>疲労)

概要

論文の詳細を見る
In order to study the mechanism of the subsurface crack initiation and propagation of high strength steel in very high-cycle region, computational simulation with fracture surface topographic analysis (FRASTA) method was carried out for specimens of high-carbon-chromium bearing steel, JIS SUJ2, obtained from the rotary-bending fatigue test in air. A remarkable area formed around the nonmetallic inclusion inside the fish-eye zone on the fracture surface, which is a feature on the fracture surface in superlong fatigue and named as GBF (granular-bright-facet), was observed in detail by a scanning probe microscope and a three-dimensional SEM. The GBF area, in which a rich carbide distribution was detected by EPMA, revealed a very rough and granular morphology in comparison with the area inside the fish eye. It was clearly simulated by the FRASTA method that multiple microcracks initiate disper-sively by the decohesion of spherical carbide from the matrix around a nonmetallic inclusion and coalesce each other into the GBF area during fatigue process. After formation of the GBF area, interior crack grew radially and the fish-eye pattern formed on the fracture surface.
社団法人日本材料学会の論文
2003-11-15