PVD法によるTiN被覆炭素鋼のフレッティング疲労特性
スポンサーリンク
概要
- 論文の詳細を見る
rights: 本文データは社団法人日本機械学会の許諾に基づきCiNiiから複製したものであるFretting fatigue tests of carbon steel coated with titanium nitride (TiN) by PVD method were carried out to discuss the effect of ceramic coating on fretting fatigue behavior. Fretting fatigue strength of the present carbon steel significantly increased by TiN coating onto the specimen. The fretting fatigue fracture process in TiN coated steel was as follows. Fretting cracks initiate at a certain stage of fatigue life from the flaws or worn region in TiN film initiated by fretting action, and propagate until final unstable fracture occurs. The improvement of fretting fatigue strength by TiN coating resulted mainly from the retardation of fretting fatigue crack initiation due to existence of hard TiN film on the contact surface of the specimen.
- 一般社団法人日本機械学会の論文
- 1999-04-25
著者
関連論文
- 338 プラズマ光輝窒化と TiN 被覆のハイブリッド表面改質処理を施した SKD61 鋼の疲労強度特性
- アルミニウム合金の疲労強度に及ぼすアルマイト被覆の影響
- アルマイト処理を施したアルミニウム合金A2014-T6の疲労強度特性
- 140 アルミニウム合金の疲労強度特性に及ぼすアルマイト処理の影響
- 多連式軸荷重疲労試験機の開発と基本性能の検証
- (4)高炭素クロム軸受鋼の超広寿命域における回転曲げ疲労特性と破面形態(論文)(日本機械学会賞〔2002年度(平成14年度)審査経過報告〕)
- 高炭素クロム軸受鋼の超広寿命域における回転曲げ疲労特性と破面形態
- プラズマ利用複合表面処理工具鋼(SKD61)の疲労強度と内部き裂進展特性
- 遮熱コーティングを施したNi基超合金の低サイクル疲労強度に及ぼす試験温度の影響
- 高炭素クロム軸受鋼のS-N曲線と内部き裂発生挙動(疲労)
- 912 WC-Co 溶射 SNCM439 鋼のフレッティング疲労特性
- 911 A6151 および A2014 アルミニウム合金の疲労特性に及ぼすショット・ピーニング処理の影響
- 910 SCM435 鋼の超長寿命疲労特性と窒化処理の影響
- PVD法によるTiN被覆炭素鋼のフレッティング疲労特性
- 110 アルミニウム合金の疲労強度特性に及ぼす冷間鍛造の影響
- 改良9Cr-1Mo鋼厚肉鍛造材の高温低サイクル疲労強度に及ぼす切欠きおよび熱時効の影響
- トポグラフィ破面解析による高強度鋼の内部疲労き裂発生・進展機構に関する研究(疲労)
- 高速度工具鋼SKH51の超長寿命域の疲労挙動に及ぼす表面処理の影響
- 高速度工具鋼SKH 51の超長寿命疲労挙動と破壊形態
- 高炭素クロム軸受鋼の超長寿命疲労挙動に及ぼす二段二重変動荷重の影響と内部き裂進展挙動
- 高炭素クロム軸受鋼の超長寿命疲労強度に及ぼすショットピーニングの影響
- 高炭素クロム軸受鋼の広寿命域における特徴的回転曲げ疲労特性に関する実験的検証
- Ti-6Al-4V 合金の高温低サイクル疲労寿命に及ぼすひずみ波形の影響
- β型チタン合金の内部疲労き裂発生挙動に及ぼす応力比の影響
- 超音波後方散乱波のウェーブレット解析による材料欠陥評価
- SKH51鋼の超長寿命域の疲労における内部疲労き裂発生・進展機構に関する破面解析的検討
- 窒化クロム被覆処理鋼の腐食疲労挙動(疲労)
- 多孔質静圧気体スラスト軸受の安定性改善について