発泡金属複合アルミニウム合金の強度特性に及ぼす化合物層の影響
スポンサーリンク
概要
- 論文の詳細を見る
This paper deals with the strength of nickel-foam reinforced aluminum Alloy (NFRA) and clarifies the indluence of the thickness of intermerallic compound layer of NFRA.NFRA has two kinds of intermerallic compound layer between nickel-foam and base metal formed by artificial aging.In order to vary the thickness of intermerallic compound layer,three different heat treatment conditions were performed on three rypes of NFRA with defferent size of Ni skeletons and on AC8A aluminum alloy.Fatigue tests and tensile tests were carried out on NFRA and AC8A aluminum alloy.The fatigue life and tensile strength of NFRA decreased significantly as compared with those of AC8A.The thickness of intermetallic compound layer affects both the fatigue strength and tensile strength,since the intermetallic compound layer changes the bonding strength of the interface between nickel-foam and base metal.
- 社団法人日本材料学会の論文
- 1993-11-15
著者
関連論文
- 炭素鋼S45C焼なまし材のねじり腐食疲労過程 : 回転曲げ腐食疲労過程との比較
- 多結晶金属材料の応力繰返しに伴う塑性変形挙動に及ぼす静水圧力の影響
- 多結晶金属材料のヒステリシスループに伴うミスオリエンテーションの変化
- 結晶の連続体近似による多結晶金属の変形応力に関する考察
- 多結晶金属材料の変形応力に及ぼす静水圧力の影響に関するX線的研究
- ミスオリエンテーションの定義とその金属材料の強度評価への応用
- 多結晶金属材料の高温クリープ変形に及ぼす静水圧応力の影響に関するX線的研究
- (3-40) 静水圧力処理を受けた多結晶金属材料の塑性変形挙動
- 多結晶金属材料の応力繰り返しに伴う塑性変形に関するX線的研究
- 塑性変形を受けた多結晶金属材料の静水圧力処理による構造変化に関するX線的研究