ゾルーゲル法によるナイロンフィルムへのシリカ薄膜の調製(<特集>高分子材料)

概要

論文の詳細を見る
Silicate layer was prepared on the nylon 6 film by sol-gel method. Effect of reaction conditions on the various properties, such as layer thickness, surface morphology and the water vapor permeation rates were examined. Increasing sol-gel reaction time gives a increasing silicate layer thickness. However because of the roughness of the surface produced due to the 3-dimensional siloxane network formation in sol-gel reaction system occurred at a longer reaction time, the water vapor permeation rate was high. Addition of DMF in sol-gel reaction system controlled the drying of coated film and suppressed the shrinkage of silicate layer resulting in the smooth crack-free layers. When UV was irradiated on the sol-gel reaction system, the surface of the coated film was rather smooth and the coated film gave a fairly high barrier to water vapor, although the thickness of the layer was rather small.
社団法人日本材料学会の論文
2002-12-15