低炭素鋼の疲労限度に及ぼす初期転位くぎ付けの影響

概要

論文の詳細を見る
The fatigue tests of a low carbon steel were made in rotatory bending at room temperature. Both annealed and strain-aged specimens were prepared to vary the effectiveness of initial dislocation locking and of strain aging for fatigue limit. The latter specimen, subjected to a cyclic stress at 375℃ prior to the test at room temperature, showed an increase in initial dislocation locking and a decrease in strain aging potential in the preliminary tensile tests. The relationship between the fatigue limit σ_<w0> and grain size d, σ_<w0>=C_w+k_wd^<-1/2>, was applied to evaluate the characteristic values C_w and k_w. The following results were obtained from the fatigue tests. (1) Both the characteristic values C_w and k_w increased with cyclic prestress at 375℃. The increases in C_w and k_w were about 7% and 65%, respectively. (2) The increase in C_w may be interpreted as a result of the increased frictional stress due to cyclic strain hardening by prestress and precipitation hardening by precipitates formed during cyclic strain aging at 375℃. (3) When k_w is regarded as a measure of barrier at grain boundary against crack-propagation of a micro-crack initiated in a grain, the increase in k_w may be attributed to the increase in initial dislocation locking rather than the effect of relocking of dislocation by cyclic strain aging. It is concluded that the initial locking of dislocations by solute atoms makes an important contribution to the existence of a fatigue limit at room temperature.
社団法人日本材料学会の論文
1983-01-15

低炭素鋼の疲労限度に及ぼす初期転位くぎ付けの影響

スポンサーリンク

概要

著者

関連論文

スポンサーリンク