高張力鋼の応力腐食割れのフラクトグラフィ的研究(<小特集>X線材料強度小特集)

概要

論文の詳細を見る
The fracture surface of stress corrosion cracking of tempered SNCM 8 steel in a 3.5% NaCl solution environment was observed by means of scanning electron microscopy and the X-ray diffraction technique. A quantitative nature of the topography and the residual stress of the fracture surface were found to be more closely related to the crack growth rate than to the stress intensity factor. The relation between the areal fraction φ of prior-austenite grain boundary fracture in the fracture surface and the growth rate da/dt of stress corrosion cracks was obtained as da/dt = exp (A - Cφ) where A is a constant dependent on tempering temperature while C is independent. The residual stress σ_R measured on the fracture surface by the X-ray method was tensile and changed as a function of the areal fraction of grain boundary fracture: σ_R= (1-φ)σ^^-R The mechanical field neat the tip of a stress corrosion crack with microbranching was modeled by a blunt crack with the equivalent root radius ρ_<eq>. The equivalent stress intensity factor given by K_<eq> = √<pl/p_<eq>> K was proposed to be a fracture mechanics parameter for characterizing the near-tip field, thus the crack growth rate. The value of p<eq> is twice the microbranching width of the crack and p_1 is the limiting root radius for a sharp crack. The concept the equivalent stress intensity factor may explain the finding that the fractographic feature is more closely related to the crack growth rate than to the stress intensity factor.
社団法人日本材料学会の論文
1979-03-15

高張力鋼の応力腐食割れのフラクトグラフィ的研究(<小特集>X線材料強度小特集)

スポンサーリンク

概要

著者

関連論文

スポンサーリンク