超音波による窒化珪素セラミックスの評価(<小特集>セラミック材料小特集)
スポンサーリンク
概要
- 論文の詳細を見る
In the hot-press sintered ceramics, their longitudinal and transverse wave velocities exhibited anisotropies characterized by the "Quasi-uniaxial symmetry" represented by the principal axis parallel to the pressure direction in hot-pressing. Velocities propagating perpendicular to the hot-press direction were somewhat faster than those propagating parallel to the hot-press direction. Velocity differences between the "parallel" and the "perpendicular" directions were estimated to be about 5% in Si_3N_4. For convenience' sake, elastic constants were evaluated from the velocity values measured in the hot-press direction. The propagation loss factors at room temperature were measured by longitudinal and transverse waves in the frequency range of 30 to 130 MHz. Loss factors exhibited the frequency dependent characteristics proportional to the square of frequency. Acoustic Emission (AE) associated with slow crack growth was observed at room temperature in the atmosphere by using the double torsion technique in which the cross-head speed of 10μ/min as adopted. A close relationship between the AE patterns and the fracture surface structure was early recognized. Averaged crack growth velocities and stress intensity factors were calculated to e l0^<-4>m/s and 5. 1×10^5kgm<-3/2>. respectively. In addition, it was confirmed that the AE count rate, dN/dt, was linearly proportional to the crack growing velocities in the range of the order of l0^<-4>m/s. The Si_3N_4 cylinder (168 mm diameter with 15 mm thickness and 93 mm axial length) with the thin hole-type-model defects processed by the laser drilling was prepared to confirm the performance of the conventional ultrasonic NDT apparatus. The sizes of the model defects were chosen as 150, 320, and 500μ. Detectability of the defects with the size of about 50μ was confirmed by echo detection due to refracted transverse waves of 5 MHz in the water immersion method.
- 社団法人日本材料学会の論文
- 1981-10-15
著者
関連論文
- 532 流れ解析の小形ファン開発への応用(GS07 熱・流動解析)
- F219 櫛型フィンの設計手法(オーガナイズドセッション22 : 熱輸送デバイス)
- 半導体パッケージ実装構造の熱・応力連成解析(OS1b 電子デバイス実装・電子材料と計算力学)
- A7 2周波数超音波プローブ
- 1)積層圧電素子を用いた超音波プローブ(情報入力研究会)
- C121 電子機器用水冷システムの放熱特性評価
- 超音波による窒化珪素セラミックスの評価(セラミック材料小特集)
- 238 Source の異なる SUS-304 材の AE 特性比較
- 31a-H-9 PZT系圧電セラミックスの分極反転に伴なうAcoustic Emission (II)
- 高温音響センサ-,AEセンサ-を中心として (最近の超音波探触子特集)
- 2a-H-2 PZT系圧電セラミックの分極反転に伴なうAcoustic Emission (II)
- 27p-W-11 PZT系圧電セラミックスの分極反転に伴うAcoustic Emission
- 超先進構造・材料としての知的材料(インテリジェント・マテリアル)-5-圧電材料
- E219 サブクール流動沸騰を用いた電子デバイスの高熱流束除熱 : 小さい流路の除熱特性(オーガナイズドセッション21 : 電子機器の熱設計と解析の応用)
- E218 サブクール流動沸騰を用いた電子デバイスの高熱流束徐熱 : 小型マルチチャンネルの除熱特性(オーガナイズドセッション21 : 電子機器の熱設計と解析の応用)
- 1825 半導体パッケージの実装構造における複合領域の信頼性解析法
- 647 パワーユニットの熱抵抗ロバスト性評価
- 音響放出センサ
- 10p-N-10 ホットプレス焼成セラミックスでの音速異方性と2,3次弾性定数
- 24p-M-6 Mn-Zn Ferrite単結晶での超音波吸収
- 24p-P-11 高圧下の超音波測定によるLiTaO_3の音響的非線形性 (II)
- 3p-Q-7 Mn-Znフェライト單結晶での超音波吸収
- 3p-C-9 高圧下の超音波測定によるLiTaO_3の音響的非線形効果
- 1p-T-8 CaTiO_3セラミックのマイクロ波誘電特性
- 超音波による材料,半導体デバイスの特性評価と品質管理 (プロセスにおけるメカニカルセンサの活用)
- 1839 次世代パワーデバイスの熱的課題
- E214 熱伝導解析によるBGAパッケージの温度予測(オーガナイズドセッション21 : 電子機器の熱設計と解析の応用)
- C124 給液促進機構を持つ狭あい流路構造による限界熱流束の増大