多孔質アルミナの力学特性に及ぼす気孔率および気孔形態の影響(<特集>セラミック材料)
スポンサーリンク
概要
- 論文の詳細を見る
Porous alumina samples were prepared with a fine alumina powder containing glass balloon or polyvinyl alcohol (PVA) as pore-former. After calcination, alumina samples with different porosities and pore morphologies were synthesized at 1623K by pressureless sintering. Referential porous alumina samples without the pore-former was obtained by reducing the sintering temperatures. Density, porosity and microstructure of porous alumina samples thus obtained were characterized. Young's modulus and Poisson's ratio were estimated by the linear strain under compressive stress and fracture strength was measured by three-point bending test. With adding the pore-former, the spherical pores with 10,20μm in diameter were observed uniformly in alumina matrix. Closed pores were predominant for porous alumina samples prepared with glass balloon, and open or continuous pores were for porous alumina samples with PVA. Continuous but small pores were mainly observed in alumina samples sintered at lower temperatures. Young's modulus of porous alumina decreased with increasing porosity, independent of pore shape and size. A slight decrease in Poisson's ratio was observed for porous alumina samples prepared with glass balloon and PVA, and a clear decrease for referential porous alumina samples sintered incompletely. The fracture strength also decreased with an increase in porosity. Especially, the continuous and large pores accompanied with sharp and large flaws were found to cause strength reduction. These mechanical properties of porous alumina were discussed in terms of power law based on the minimum solid segment or area model.
- 社団法人日本材料学会の論文
- 2001-06-15
著者
-
西川 直宏
名古屋工業大学極微構造デバイス研究センター
-
本多 沢雄
名古屋工業大学材料工学科
-
淡路 英夫
名古屋工業大学材料工学科
-
淡路 英夫
名古屋工業大学大学院 物質工学専攻
-
本多 沢雄
名古屋工大
-
本多 沢雄
名古屋工業大学大学院
-
中嶋 篤久
名古屋工業大学材料工学科
-
淡路 英夫
名古屋工業大学大学院物質工学専攻
-
Awaji Hideo
Nagoya Institute Of Technology
-
西川 直宏
名古屋工業大学材料工学科
-
西川 直宏
名古屋工業大学
-
本多 沢雄
名古屋工業大学 環境材料工学科
-
本多 沢雄
名古屋工業大学
-
淡路 英夫
名古屋工業大学名誉教授
関連論文
- Si基板上GaN系発光ダイオードの結晶成長及び諸特性
- 高熱伝導窒化ケイ素の熱衝撃特性評価
- 窒化ケイ素の熱衝撃破壊靱性評価
- C-4-34 Si基板上InGaN MQW LEDの作製
- 酸化マグネシウムを部分固溶した酸化亜鉛粉末の作製とカソードルミネセンス
- セラミックス円板の水中急冷熱衝撃試験
- Al-Si-C系複合炭化物の焼結と機械的特性
- 322 セラミック基ナノ複合材料 : 新しい材料設計概念(MMC・CMC,複合材料の開発・応用・評価における新技術,オーガナイスドセッション6,第53期学術講演会)
- 拘束したスラブの一面加熱によるセラミックスの熱破壊じん性の測定
- 急冷されるセラミック円板の熱応力解析