The size of the frontal process-zone at the crack tip of ceramics is an important factor to assess the toughening mechanisms operative in the material. An indirect technique is proposed here to estimate the critical size of the frontal process zone in ceramics using a single-edge V-notched beam (SEVNB) method. A three-point flexure test was carried out on alumina specimens containing a sharp V-shaped notch whose depth was varied. Then, a critical local stress was calculated at a critical distance from the notch tip. The frontal processzone size at the beginning of crack propagation, namely, the critical frontal process-zone size, was determined as the distance between the notch tip and the point where the critical local stress has the same value as the flexural strength of the specimen. This concept is based on a local fracture criterion. The calculated critical frontal process-zone size of alumina ceramics was 11.4μm based on the linear elasticity, and 22.8μm based on the Dugdale model.
- 社団法人日本セラミックス協会の論文
- 2001-07-01
著者
-
淡路 英夫
名古屋工業大学材料工学科
-
淡路 英夫
名古屋工業大学大学院 物質工学専攻
-
崔 成〓
名古屋工業大学大学院物質工学専攻
-
淡路 英夫
名工大
-
Jayaseelan Daniel
産業技術総合研究所
-
淡路 英夫
名古屋工業大学大学院物質工学専攻
-
Awaji Hideo
Nagoya Institute Of Technology
-
崔 成〓
名古屋工業大学大学院工学研究科物質工学専攻材料力学物性研究室
-
淡路 英夫
名古屋工業大学名誉教授
関連論文
- 高熱伝導窒化ケイ素の熱衝撃特性評価
- 窒化ケイ素の熱衝撃破壊靱性評価
- セラミックス円板の水中急冷熱衝撃試験
- 322 セラミック基ナノ複合材料 : 新しい材料設計概念(MMC・CMC,複合材料の開発・応用・評価における新技術,オーガナイスドセッション6,第53期学術講演会)
- アルミナ基高靭性ナノ複合材料の作製(イノベーティブセラミックス(I))
- 1K09 PECS 法で作製したアルミナ/コバルトナノ複合材料の機械的特性
- 脆性材料の強度と破壊靱性の関係
- カーボン含有耐火物の直接通電加熱法と全面加熱法による熱衝撃試験の比較
- 吹き付けアモサイトの無害化
- アスベストを含む廃建材の無害化とセメント製品への適用