Bi-Sr-Ca-Cu-O系超伝導体におけるゼーベック係数, 酸素含有及び超伝導特性の相関

概要

論文の詳細を見る
The correlations among Seebeck coefficient, oxygen content and superconducting property ware examined for four Bi-Sr-Ca-Cu-O systems, i.e., a 2223-phase oxide, Bi_<1.84>Pb_<0.34>Sr_<1.91>Ca_<2.03>Cu_<3.06>O_<10.1-z>and three 2212-isostructural oxides, Bi_2Sr_<2-x>Ca_<1+x>Cu_2O_y(x=0, 0.5 and 1.0). Temperature-Programmed-Desorption(TPD)as well as Temperature-Programmed-Oxidation(TPO)measurements revealed that small amounts of oxygen(2-3×10^<-5>mol/g)were sorbed and desorbed reversibly for all oxides examined in the temperature ranges of ca. 100-400℃ and ca. 250-600℃, respectively. In good agreement with such sorption-desorption behavior, the Seebeck coefficient (Q) of each oxide was found to change reversibly with changing temperature in the range of 100-600℃. This means that Q is a reversible function of oxygen content for each oxide. For the 2212-oxides, Q values at 100℃ were in the range of ca. -10-+10μV/K and increased to the positive direction almost linearly with decreasing oxygen content, though the increments were somewhat different depending on composition. This indicates that oxygen content is directly related with the carrier concentration of each sample. Interestingly, T_c of each 2212-oxide was observed to go through a maximum with oxygen content. It was found that the highest T_c was reached at the oxygen content at which Q was brought to around zero at 100℃ for each oxide. These results suggest that there exists an optimum carrier concentration giving the highest T_c in common for the three 2212-oxides tested.
社団法人日本セラミックス協会の論文
1995-02-01

Bi-Sr-Ca-Cu-O系超伝導体におけるゼーベック係数, 酸素含有及び超伝導特性の相関

スポンサーリンク

概要

著者

関連論文

スポンサーリンク