ほうろうに関する界面物理化学的研究(第3報) : ほうろう界面に及ぼすコバルトの作用

概要

論文の詳細を見る
The effect of cobalt on enamel reaction was studied using Co-vitreous enamel. Observation and analysis of Co-vitreous enamel interface were performed with scanning electron microscope, X-ray photoelectron spectrometer and X-ray diffractometer. The following results were obtained. (1)The sunken parts of Co-vitreous enamel interface were formed by erosion of the base iron. Cobalt and iron deposited on the base iron and formed convex parts. Further, the convex parts grew by firing from the initial interface towards the glass(enamel layer)side. (2)Interface layer of Co-vitreous enamel was consisted of two layers. The first interface layer was very thin and consisted of CoFe_2O_4 or FeFe_2O_4. The second interface layer was the iron solid solution containing cobalt. The thickness of Co-vitreous enamel reaction layer was thicker than the rough parts. (3)The Co-vitreous enamel reaction was a galvanic cell reaction between base iron and cobalt ion in glass. Cobalt circulate by reaction as deposition, oxidation and dissolution.
社団法人日本セラミックス協会の論文
1999-03-01