高マンガン大洲田鋼の加熱による組織及性質の變化
スポンサーリンク
概要
- 論文の詳細を見る
A high manganese austenitic steel with 12.74%Mn and 1.19%C, obtained by quenching in water from 1000°, was heated at several temperatures from 400° to 700°, for various lengths of time upto 50 hours, during which the change of microstructure, density, hardness and magnetization was studied. In microstructure, the following changes take place : -(1) separation of carbide, (2) formation of troostite (nodulus), (3) formation of martensite, (4) formation of troostite (acicular) from martensite. The separation of carbide firstly takes place ; as the heating temperature rises, the rate of separation increases, though the quantity of the carbide decreases, on account of an increase of the solubility. The formation of troostite (nodulus) and martensite take place in temperature ranges, 420°∿680°, and 420°∿600°, respectively ; in the early stage of heating, the changes proceed most readily in the vicinity of 550°, and as the heating time increases, the temperature at which the change is maximum shifts gradually to the lower temperature. The acicular troostite is formed in the temperatures above 500° from the martensite. The density increases with the separation of carbide and the formation of troostite, but decreases with that of martensite. The hardness increases with the formation of carbide and martensite, but decreases with that of troostite. Magnetization increases with the format on of martensite and troostite, though no change is observable with the separation of carbide. From these facts the process of tempering of the austenite at several temperatures was inferred. The troostites, nodulus and acicular, are formed by different mechanism, that is, the former is formed by the Ar_1 change as the pearlite, while the latter is formed by tempering of martensite after long heating. According to Tammann's theory, the experimental results obtained were well explained. By means of the differential dilatometer, the Ac_1 range was determined to be 530°∿680°.
- 社団法人日本鉄鋼協会の論文
- 1931-03-25
著者
関連論文
- タングステン鋼に於ける針状地鐵の生成に就いて
- 13) タングステン鋼の組織に就て(日本鐵鋼協會第二囘講演大會)
- 高マンガン高クロム大洲田鋼の高温特性に及ぼす各種元素の影響に就て
- 鋼の燒入硬化に及ぼす特殊元素の影響 (II)
- マンガン鋼の顯微鏡組織圖研究補遺
- 鋼の燒入硬化に及す特殊元素の影響 (I)
- 20) 鋼の燒入効果に及す特殊元素の影響(日本鐵鋼協會第拾囘講演大會)
- 高マンガン大洲田鋼の加熱による組織及性質の變化
- マンガン鋼の變態點及顯微鏡組織
- 炭素鋼の滲炭及脱炭に就いて
- 高速度鋼の燒入組織に及ぼす酸化脱炭の影響
- 7) 高速度鋼の燒入組織に及ぼす酸化脱炭の影響(日本鐵鋼協會第拾四囘講演大會)
- 鋼の燒入膨脹速度に及ぼす諸元素の影響
- 19) 鋼の燒入膨脹速度に及ぼす特殊元素の影響(日本鐵鋼協會第拾壹囘講演大會)
- 講演会の今昔(3.1 思い出, 3. 回顧と将来の展望, I. 日本鉄鋼協会 50 年史)
- 鋼の品質と微量成分
- 調質鋼板熔接ビード割れの発生頻度に及ぼす大洲田鋼型電極棒心線の化学組成の影響
- ニッケル・クロム鋼の變態速度に就て
- 15) ニッケル-クロム鋼の變態速度に就て(日本鐵鋼協會第拾八囘講演大會)
- クロム鋼の冷却條件による變態點及び顯微鏡組織の變化
- 26) クロム鋼の冷却條件による變態點及顯微鏡組織の變化(日本鐵鋼協會第拾囘講演大會)
- 高滿俺大洲田鋼の加熱變化に及ぼす炭素の影響
- クロム鋼の組織成分に就て
- モリブデン鋼に於ける變態點の降下に就て
- クロム鋼の組織圖
- 19) 鐵-炭素-クローム系合金の組織に就て(日本鐵鋼協會第三囘講演大會)