Utilizing the Magnetic analysis with specimens of less than 27.8% Cr and 1.55% C, the change of the transformation point due to the cooling conditions was studied, and several diagrams showing the composition range in which the transformation is lowered and its change due to the cooling conditions were proposed. The microstructure of these specimens and its change due to the cooling conditions were examined, and structural diagrams showing the relation between the composition of specimens and the microstructures in 4 cases cooled from 900° and 1, 100° in furnace and in air, respectively were constructed. Based on these diagrams the effects of carbon and chromium contents in specimens, the cooling rate and the maximum heating temperature on the microstructure were elucidated. By examining the microstructure of several specimens which were carburized and cooled under several conditions the effect of carbon on the microstructure was studied, and the correctness of the structural diagrams obtained above was confirmed.
- 社団法人日本鉄鋼協会の論文
- 1934-11-25
著者
関連論文
- タングステン鋼に於ける針状地鐵の生成に就いて
- 13) タングステン鋼の組織に就て(日本鐵鋼協會第二囘講演大會)
- 高マンガン高クロム大洲田鋼の高温特性に及ぼす各種元素の影響に就て
- マンガン鋼の顯微鏡組織圖研究補遺
- 高マンガン大洲田鋼の加熱による組織及性質の變化
- マンガン鋼の變態點及顯微鏡組織
- 炭素鋼の滲炭及脱炭に就いて
- 高速度鋼の燒入組織に及ぼす酸化脱炭の影響
- 7) 高速度鋼の燒入組織に及ぼす酸化脱炭の影響(日本鐵鋼協會第拾四囘講演大會)
- 鋼の燒入膨脹速度に及ぼす諸元素の影響
- 19) 鋼の燒入膨脹速度に及ぼす特殊元素の影響(日本鐵鋼協會第拾壹囘講演大會)
- 講演会の今昔(3.1 思い出, 3. 回顧と将来の展望, I. 日本鉄鋼協会 50 年史)
- 鋼の品質と微量成分
- 調質鋼板熔接ビード割れの発生頻度に及ぼす大洲田鋼型電極棒心線の化学組成の影響
- ニッケル・クロム鋼の變態速度に就て
- 15) ニッケル-クロム鋼の變態速度に就て(日本鐵鋼協會第拾八囘講演大會)
- クロム鋼の冷却條件による變態點及び顯微鏡組織の變化
- 26) クロム鋼の冷却條件による變態點及顯微鏡組織の變化(日本鐵鋼協會第拾囘講演大會)
- 高滿俺大洲田鋼の加熱變化に及ぼす炭素の影響
- クロム鋼の組織成分に就て
- モリブデン鋼に於ける變態點の降下に就て
- クロム鋼の組織圖
- 19) 鐵-炭素-クローム系合金の組織に就て(日本鐵鋼協會第三囘講演大會)
- 鼠銑鑄物の熱處理に依る機械的性質と顯微鏡組織の變化