クロム鋼の組織圖
スポンサーリンク
概要
- 論文の詳細を見る
The microstructure of chromium steels markedly changes, according to the composition and the coolling condition, i.e. maximum heating temperature and cooling rate. Studying the microstructure for 46 specimens of chromium steels containing less than 28 percent of chromium and 1.6 percent of carbon, cooled under the following conditions, the structural diagrams for the respective cases were constructed : -(1) very slowly cooled from 900°, (2) cooled in furnace from 900°, (3) cooled in air from 900°, (4) cooled in furnace from 1200°, and (5) cooled in air from 1200°. In these diagrams the composition range of steels showing the self-hardening property is clearly shown. Moreover, from these diagrams, the following facts are concluded : -(1) the carbon content at the eutectoid points and the solubility of carbon at the eutectic point decreases, as the chromium content increases : (2) the pearlitic region in the normal structure increases, as the carbon content increases : (3) When the cooling condition is equal, the microstructure changes from pearlite or troostite to martensite and austenite in addition of chromium, and in further increasing chromium, ferrite containing high chromium appears : (4) As the cooling rate increases, or the maximum heating temperature rises, martensite or austenite readily appears, pearlite or troostite tending to be hardly formed : (5) In high carbon alloys, the martensite or austenite hardly appears, unless the cooling rate is rapid or the maximum heating temperature is high ; as the cooling rate and the maximum temperature increases, the austenite is easily retained.
- 社団法人日本鉄鋼協会の論文
- 1928-02-25
著者
関連論文
- タングステン鋼に於ける針状地鐵の生成に就いて
- 13) タングステン鋼の組織に就て(日本鐵鋼協會第二囘講演大會)
- 高マンガン高クロム大洲田鋼の高温特性に及ぼす各種元素の影響に就て
- マンガン鋼の顯微鏡組織圖研究補遺
- 高マンガン大洲田鋼の加熱による組織及性質の變化
- マンガン鋼の變態點及顯微鏡組織
- 炭素鋼の滲炭及脱炭に就いて
- 高速度鋼の燒入組織に及ぼす酸化脱炭の影響
- 7) 高速度鋼の燒入組織に及ぼす酸化脱炭の影響(日本鐵鋼協會第拾四囘講演大會)
- 鋼の燒入膨脹速度に及ぼす諸元素の影響
- 19) 鋼の燒入膨脹速度に及ぼす特殊元素の影響(日本鐵鋼協會第拾壹囘講演大會)
- 講演会の今昔(3.1 思い出, 3. 回顧と将来の展望, I. 日本鉄鋼協会 50 年史)
- 鋼の品質と微量成分
- 調質鋼板熔接ビード割れの発生頻度に及ぼす大洲田鋼型電極棒心線の化学組成の影響
- ニッケル・クロム鋼の變態速度に就て
- 15) ニッケル-クロム鋼の變態速度に就て(日本鐵鋼協會第拾八囘講演大會)
- クロム鋼の冷却條件による變態點及び顯微鏡組織の變化
- 26) クロム鋼の冷却條件による變態點及顯微鏡組織の變化(日本鐵鋼協會第拾囘講演大會)
- 高滿俺大洲田鋼の加熱變化に及ぼす炭素の影響
- クロム鋼の組織成分に就て
- モリブデン鋼に於ける變態點の降下に就て
- クロム鋼の組織圖
- 19) 鐵-炭素-クローム系合金の組織に就て(日本鐵鋼協會第三囘講演大會)