鋼の燒入膨脹速度に及ぼす諸元素の影響
スポンサーリンク
概要
- 論文の詳細を見る
A self-recording apparatus of expansion-time curve during quenching of steel was constructed. With this apparatus, the expansion-time curve was obtained for 4 carbon steels and 32 steels containing less than 2% of Mn, Ni, Co, V, Cr, Si, W or Mo with nearly eutectoid carbon content. The quenching temperature varied from 850℃ to 1, 100℃, the quenching medium being oil. The velocity of expansion due to martensitization was calculated by the following formula, dx/dt=K (a-x, in which x shows the amount of martensite formed at time, t, a amount of martensite after cooled to room temperature, and K a constant. Then, the velocity of marten-sitization is shown by dx/dt=1/2・Ka, when x is 1/2・a By the value 1/2・Ka the effects of special elements and quenching temperature on the velocity of expansion were studied. The values 1/2・Ka and a change with the rise of quenching temperature, the maximum value being the case quenched from 900∿1, 000℃ The beginning temperature of martensitization generally falls, as the quenching temperature rises. In the plain carbon steel of nearly eutectoid composition the martensite is formed by oil-quenching, while in those of the hyper-and hypo-eutectoid composition the troostite is formed by the same operation. In alloy steels tested in the present work, the martensitization takes place on quenching in oil, except in 1.94% cobalt steel. The velocity and amount of expansion of vanadium steels are small and those of tungsten steels are large. Among the steels containing 0.5 and 1% of special element added, manganese steel has the largest, velocity of expansion, while among those with 1.5% or 2% of special element, tungsten steel is the largest.
- 社団法人日本鉄鋼協会の論文
- 1934-09-25
著者
関連論文
- タングステン鋼に於ける針状地鐵の生成に就いて
- 13) タングステン鋼の組織に就て(日本鐵鋼協會第二囘講演大會)
- 高マンガン高クロム大洲田鋼の高温特性に及ぼす各種元素の影響に就て
- マンガン鋼の顯微鏡組織圖研究補遺
- 高マンガン大洲田鋼の加熱による組織及性質の變化
- マンガン鋼の變態點及顯微鏡組織
- 炭素鋼の滲炭及脱炭に就いて
- 高速度鋼の燒入組織に及ぼす酸化脱炭の影響
- 7) 高速度鋼の燒入組織に及ぼす酸化脱炭の影響(日本鐵鋼協會第拾四囘講演大會)
- 鋼の燒入膨脹速度に及ぼす諸元素の影響
- 19) 鋼の燒入膨脹速度に及ぼす特殊元素の影響(日本鐵鋼協會第拾壹囘講演大會)
- 講演会の今昔(3.1 思い出, 3. 回顧と将来の展望, I. 日本鉄鋼協会 50 年史)
- 鋼の品質と微量成分
- 調質鋼板熔接ビード割れの発生頻度に及ぼす大洲田鋼型電極棒心線の化学組成の影響
- ニッケル・クロム鋼の變態速度に就て
- 15) ニッケル-クロム鋼の變態速度に就て(日本鐵鋼協會第拾八囘講演大會)
- クロム鋼の冷却條件による變態點及び顯微鏡組織の變化
- 26) クロム鋼の冷却條件による變態點及顯微鏡組織の變化(日本鐵鋼協會第拾囘講演大會)
- 高滿俺大洲田鋼の加熱變化に及ぼす炭素の影響
- クロム鋼の組織成分に就て
- モリブデン鋼に於ける變態點の降下に就て
- クロム鋼の組織圖
- 19) 鐵-炭素-クローム系合金の組織に就て(日本鐵鋼協會第三囘講演大會)