酸素上吹き溶銑精錬時の Na_2CO_3 スラグの特性

概要

論文の詳細を見る
Change in chemical composition of slag during the refining of hot metal with Na_2CO_3 under the condition of top-oxygen blowing in the temperature range from 1280 to 1450℃ was studied. Violent decomposition of Na_2CO_3 in the presence of [C] was observed at the beginning of experiments. However, total amount of Na evaporated from slag during the experiment was not conspicuous. Rate of vaporization of Na was found to decrease with decreasing reaction temperature and with increasing contents of acidic compounds in the slag, such as SiO_2 and P_2O_5. Judging from material balance calculation for S, some part of charged S was considered to be transferred to waste gas. Chemical analysis of the dust and slag indicated that the preferential vaporization of S and Na from the slag occurred. Vaporization loss of P was not detected by chemical analysis of dust and slag. However, the study with thermal-balance showed that Na_3PO_4 reacted readily with graphite and converted to CO, P and Na above 1000℃.
社団法人日本鉄鋼協会の論文
1983-01-01