γ型 Fe-Co-Cr-Ni 基耐熱合金, LCN-155 の焼戻による物理的性質の変化 : γ型耐熱合金の焼戻過程に関する研究 I

概要

論文の詳細を見る
The tempering process of the solution-treated γ type heat-resisting alloy consisting mainly of Fe, Co, Cr and Ni, and the effects of solution-treating temperatures and the additional elements (C, N, Mo, W and Cb) on its process were investigated by measurements of dilatation, specific heat, electrical resistance, and hardness. These results were summarized as follows : 1. The tempering process of this alloy quenched in water from an elevated temperature was divided into two distinct stages about at 500° and 750℃. 2. At the first stage, an increase of electrical resistance, an evolution of heat, a contraction of the length, and no marked change of hardness were observed. It was considered that the change in properties during the first stage of tempering was not due to a precipitation of carbide or nitride but due to an unknown change in the Fe-Co-Cr-Ni quaternary alloy containing of no additional elements. 3. At the second stage, a decrease of electrical resistance, an evolution of heat, a contraction of the length, and remarkable change of hardness were observed. The change in properties during this second stage of tempering was obviously due to the precipitation of carbides, nitrides, and intermetallic compounds. The amount of these precipitates and the velocity of precipitation were remarkably affected with the additional elements and the solution-treating temperatures. 4. It was considered that the change of the first stage advanced in processes as follows : Room temp. 500℃ 650℃ In quenching states……… A⇾A⇾A′⇾A⇾A A : A stable state at high temp. 650℃ In annealing states……… A′⇄A′⇄A′⇄A⇄A A′ : A stable state at low temp.
社団法人日本鉄鋼協会の論文
1961-02-01

γ型 Fe-Co-Cr-Ni 基耐熱合金, LCN-155 の焼戻による物理的性質の変化 : γ型耐熱合金の焼戻過程に関する研究 I

スポンサーリンク

概要

著者

関連論文

スポンサーリンク