新冷却法による熱延複合組織鋼板の製造(製造技術)(<特集>高強度薄鋼板)

概要

論文の詳細を見る
For the purpose of developing the as-hot-rolled dual phase sheet steel, hot rolling conditions and subsequent cooling pattern were investigated by using 1%Si-1.5%Mn-1.0%Cr steels with carbon contents of 0.05%C and 0.08% and 0.05%C-1.0%Si-1.5%Mn steel. In order to study the exact transformation behavior immediately after finish-rolling, hot-rolled strips of these steels were stopped on the runout table and water-cooled and/or air-cooled to room temperature. This unique experiment exhibited that the optimum cooling pattern consisted of three stages ; 1) rapid cooling to a suitable temperature (∿700℃) to increase ferrite nucleation sites, 2) holding at the temperature (∿700℃) to enhance ferrite transformation, thereby stabilizing untransformed austenite due to C and N concentration, and 3) rapid cooling to a coiling temperature to avoid the formation of pearlite and bainite. Experimental rolling was performed at the production mill. The steels obtained showed dual phase structure with excellent tensile properties in terms of low yield to tensile strength ratio and high ductility.
社団法人日本鉄鋼協会の論文
1982-07-01