Application of Fiber Recovered from Scrapped FRP to Discontinuous Fiber Reinforced Mortar
スポンサーリンク
概要
- 論文の詳細を見る
This paper describes methods to make effective use of the scrapped Fiber Reinforced Plastics (FRP) for admixture of mortar and concrete. The mixing method and the flexural property of discontinuous fiber reinforced mortar used the glass fiber which was reproduced by to reclaim and decompose the scrapped FRP with the aerial palverizer were experimentally investigated. From this experiment it was found that the flexural strength and the toughness of mortar were improved with increase of the fiber content.
- 東海大学の論文
著者
-
Kikumoto Yukio
Department Of Civil Engineering
-
Kasai Tetsurou
Department Of Civil Engineering
-
Takenaka Hiroshi
Course Of Civil Engineering
関連論文
- Effect of Curing Temperature and Mineral Composition on Chemical Shrinkage of Portland Cement Paste
- Experimental Study on the Bleeding Method on Chemical Shrinkage of Portland Cement Paste
- Effects of Temperature on Rheology of Fresh Cement Paste in High-Flowing Concrete
- Study on Estimation of Densest Packing for Cement-Silica Fume Powder
- A Consideration in Countermeasure on Reduction of Road Construction Cost
- Effects of Moisture Condition of Lightweight Aggregate and Curing Condition on Shrinkage Properties of Lightweight Aggregate Concrete
- Properties of Compressive Strength and Frost Resistance Regard with Concrete Using Lightweight Aggregate of Low Absorption
- Analyses of Cement Paste Flow through a Circular Tube
- Effects of Penetration of Curing Water on Self-Desiccation and Strength ofCementitious Materials
- Effects of Penetrative Conditions of Water for Curing on The Degree of Hydration and Content of Non-evaporable Water of Hardened Cement Paste(SCHOOL OF ENGINEERING)
- Application of Fiber Recovered from Scrapped FRP to Discontinuous Fiber Reinforced Mortar
- Effects of Penetrative Conditions of Water for Curing on The Degree of Hydration and Content of Non-evaporable Water of Hardened Cement Paste(ABSTRACTS OF PROCEEDINGS OF THE SCHOOL OF ENGINEERING SERIES J TOKAI UNIVERSITY : 2002-2003)
- Effects of Water Cementitious Material Ratio and Volume Fraction of Fine Aggregates on Plastic Shrinkage of Mortar(ABSTRACTS OF PROCEEDINGS OF THE SCHOOL OF ENGINEERING SERIES J TOKAI UNIVERSITY -2003-2004-)