Carbon black (CB)-filled composites of polyethylene (PE), polypropylene (PP), and PP/PE blend with weight composition of 40/60 have been prepared by twin screw extruder, and their electrical resistivities have been investigated. In order to improve the surface properties of CB, γ-aminopropyl trimethoxysilane (APS) was used for the surface treatment of CB. The surface treatment of CB by APS was found to effectively decrease percolation threshold, φc, i.e., the electrical resistivity showed drastic decrease when the CB content was larger than φ c. Temperature dependence of APS-treated CB/PP/PE composites exhibited almost constant electrical resistivity (~106 Ωcm) in the range of 25-130°C, and it was increased drastically to ~1012Ωcm above the melting temperature of PE, resulting high positive temperature coefficient (PTC) intensity (ca. 106). This high resistivity was maintained even at the higher temperature than 150°C, and only weak negative temperature coefficient (NTC) behavior was observed. The surface treatment of CB by APS is effective to obtain CB/PP/PE composites having excellent thermal electrical property as a switching material.
- 2004-06-15
著者
-
高橋 清久
名古屋工業大学材料工学科
-
稲葉 光治
名古屋工業大学材料工学科
-
永田 謙二
名古屋工業大学大学院工学研究科
-
猪股 克弘
名古屋工業大学材料工学科
-
木村 嘉宏
名古屋工業大学材料工学科
-
永田 謙二
名古屋工大 大学院工学研究科
-
高橋 清久
名古屋工業大学
-
永田 謙二
名古屋工業大学
-
高橋 清久
都市循環システム工学専攻
関連論文
- カーボンブラック充填ポリプロピレン/ポリエチレンポリマーブレンドの電気抵抗率に及ぼす表面処理の影響
- アミノシラン処理カーボンブラック充填PP/PE複合材料の電気抵抗率とその温度特性
- カーボンブラック充填PE及びPPの電気抵抗率に及ぼす無水マレイン酸変性の影響
- ポリプロピレン/ポリエチレンポリマーブレンド中でのカーボンブラックの局在化と電気抵抗率
- カーボンブラック充填 PP/PE ポリマーブレンドの成形手順と電気抵抗率
- プラスチック廃棄物再生利用のための繊維化及び複合化技術
- 熱可塑性樹脂の繊維化と古紙とのリサイクル複合材料の試作及び力学特性
- 空調機の廃熱を利用する給湯システムの性能評価(熱工学,内燃機関,動力など)
- HFC冷媒を充填した空調機における非相溶性冷凍機油の循環観察(熱工学,内燃機関,動力など)
- 追設凝縮器を用いた空調機の運転(熱工学,内燃機関,動力など)