Phosphorous Partition in Dephosphorization Slag Occurring with Crystallization at Initial Stage of Solidification
スポンサーリンク
概要
- 論文の詳細を見る
Basicity and the amount of FetO were investigated for their effects on the crystallization behavior of the simulated dephosphorizing slags. Twelve kinds of slags were prepared (C/S=1.0–2.5, FetO=10–20%, P2O5=5%). In the present experiment, the Hot Thermocouple Technique was used to melt and quench the samples. After quenching, the microstructure of the slag and the distributions of elements were examined by SEM and EDS analysis.The diameter of the crystal which precipitated in the sample increased with increasing basicity (C/S) and decreasing FetO content. In addition, glassy regions were observed in the two samples whose FetO content was 20% and whose basicity was 1.0 or 1.5. The samples (10% FetO, 5% P2O5), whose basicity was 1.0 (sample-1) precipitated as a monocalcium silicate (CaO·SiO2); the sample (10% FetO, 5% P2O5) whose basicity was 1.5 (sample-4) precipitated as a dicalcium silicate (2CaO·SiO2). In higher FetO (15–20%) slags, the crystals of the solid solution between 3CaO·P2O5 and 2CaO·SiO2 ((C3P–C2S)ss) were observed. When the amount of CaO increased from C/S=1.5 to C/S=2.5, 2CaO·SiO2 appeared with phosphorous content, but phosphorous was not found in CaO·SiO2.
- 社団法人 日本鉄鋼協会の論文
- 2008-09-15
著者
-
Kashiwaya Yoshiaki
Graduate School of Engineering, Hokkaido University
-
Kashiwaya Yoshiaki
Graduate School Of Engineering Hokkaido University
-
Son Pham
Graduate School Of Engineering Hokkaido University
-
Kashiwaya Yoshiaki
Graduate School Of Energy Science And Technology Kyoto University
関連論文
- Latent Heat of Amorphous Slags and Their Utilization as a High Temperature PCM
- Mechanism of the Formation of Slag Particles by the Rotary Cylinder Atomization
- Development of a Rotary Cylinder Atomizing Method of Slag for the Production of Amorphous Slag Particles
- Crystallization Behaviors Concerned with TTT and CCT Diagrams of Blast Furnace Slag Using Hot Thermocouple Technique
- Analysis of the Transition State of the Carbon and Iron Oxide Mixture Activated by Mechanical Milling
- Phosphorous Partition in Dephosphorization Slag Occurring with Crystallization at Initial Stage of Solidification
- Crystallization Behaviors Concerned with TTT and CCT Diagrams of Blast Furnace Slag Using Hot Thermocouple Technique
- Quantitative Estimation of Coupling Phenomenon between Reduction and Gasification on the Facing Pair of Iron Oxide and Graphite
- Characteristics of Nano-reactor and Phenomena during Mechanical Milling of Hematite-Graphite Mixture
- Gas Evolution during Mechanical Milling of Hematite-Graphite Mixture
- Intensive Improvement of Reduction Rate of Hematite-Graphite Mixture by Mechanical Milling
- Reaction Behavior of Facing Pair Between Hematite and Graphite: A Coupling Phenomenon of Reduction and Gasification
- In Situ Observation of Reduction Behavior of Hematite with Solid Carbon and Crystallographic Orientation between Hematite and Magnetite
- Simulation Test for Crystallization of Inclusions in Semi-killed Steels during Heat Treatment Prior to Hot Rolling
- Catalytic Effect of Slags on the Formation of Biodiesel Fuel
- In Situ Observation of Diamond Gasification and the Crystallographic Relationship of Graphite Formed on the Surface of Diamond
- Kinetic Analysis of the Gasification of Diamond
- Latent Heat of Amorphous Slags and Their Utilization as a High Temperature PCM
- Effect of Oxides and Carbonate on the Reaction of Hematite and Graphite Mixture Obtained by the Mechanical Milling
- Mechanism of the Formation of Slag Particles by the Rotary Cylinder Atomization
- Development of a Rotary Cylinder Atomizing Method of Slag for the Production of Amorphous Slag Particles
- Thermodynamic Analysis on the Dust Generation from EAF for the Recycling of Dust
- Binding Energy of Carbon Implanted into Hematite and in situ Observation of Reaction Behavior during Heating Up Experiment
- Effect of Sulfur on the TTT Diagram of CaO–Al2O3 Slag at Eutectic Composition
- Atmosphere Controlled Hot Thermocouple Method and Crystallization Phenomenon of CaO–Al2O3 Eutectic Slag
- Kinetic Analysis of the Decomposition Reaction of CH4 Injecting into Molten Slag
- Thermodynamics of Impurities in Pure Iron Obtained by Hydrogen Reduction
- Simulation of Blast Furnace Operation with Intensive Hydrogen Injection
- Thermodynamics of Impurities in Pure Iron Obtained by Hydrogen Reduction
- Preface to the Special Issue on "Green Energy Ironmaking and Steelmaking –Production of Green Energy and Its Use in Ironmaking and Steelmaking–"