Effect of Sulfur on the TTT Diagram of CaO–Al2O3 Slag at Eutectic Composition
スポンサーリンク
概要
- 論文の詳細を見る
It is important to know the behavior of inclusion in a CaO-Al2O3-(SiO2 and/or MgO) system for controlling the properties of steel. The crystallization of inclusion has a large effect on the rolling process. However, there is little study of the effect of sulfur on the crystallization of inclusion. In the previous paper, the authors were investigated the sulfur behavior in the CaO-Al2O3 slag at the eutectic composition (CAEU) under controlled atmosphere. In the present study, the effects of sulfur on the TTT diagrams were measured by the hot thermocouple method under controlled atmosphere. 1 mass%, 5 mass% and 10 mass% CaS were added to the eutectic composition of calcium aluminate (CAEU). The crystal region in TTT diagrams was expanded by the addition of CaS from 1 mass% to 10 mass% under Ar atmosphere. And the start of crystallization became faster with the increase of CaS addition. The crystal phases were monocalcium aluminate (CA) and tricalcium aluminate (C3A) regardless to the CaS content. However, primary crystal was changed from the content of CaS. When 1 mass%CaS was added to CAEU, the primary crystal was CA. On the other hand, the primary crystal was C3A in the cases of 5 mass% and 10 mass%CaS.
- 2011-12-15
著者
-
Suzuki Ryosuke
Graduate School Of Science And Technology Niigata University
-
Kashiwaya Yoshiaki
Faculty Of Engineering Hokkaido University
-
Kashiwaya Yoshiaki
Div. Of Materials Sci. Graduate School Of Engineering Hokkaido Univ.
-
Kashiwaya Yoshiaki
Graduate School Of Energy Science And Technology Kyoto University
-
KUSADA Yasuaki
Graduate School of Eng., Hokkaido University
-
Suzuki Ryosuke
Graduate School Of Eng. Faculty Of Engineering Hokkaido University
関連論文
- An Investigation of the Crystallization of a Continuous Casting Mold Slag Using the Single Hot Thermocouple Technique
- Development of Double and Single Hot Thermocouple Technique for in situ Observation and Measurement of Mold Slag Crystallization
- Analysis of the Transition State of the Carbon and Iron Oxide Mixture Activated by Mechanical Milling
- Phosphorous Partition in Dephosphorization Slag Occurring with Crystallization at Initial Stage of Solidification
- Crystallization Behaviors Concerned with TTT and CCT Diagrams of Blast Furnace Slag Using Hot Thermocouple Technique
- Quantitative Estimation of Coupling Phenomenon between Reduction and Gasification on the Facing Pair of Iron Oxide and Graphite
- Characteristics of Nano-reactor and Phenomena during Mechanical Milling of Hematite-Graphite Mixture
- Gas Evolution during Mechanical Milling of Hematite-Graphite Mixture
- Intensive Improvement of Reduction Rate of Hematite-Graphite Mixture by Mechanical Milling
- Reaction Behavior of Facing Pair Between Hematite and Graphite: A Coupling Phenomenon of Reduction and Gasification