RTGG法による結晶配向性CaBi_4Ti_4O_<15>およびSrBi_4Ti_4O_<15>の作製におけるヘテロ凝集の影響
スポンサーリンク
概要
- 論文の詳細を見る
Textured CaBi4Ti4O15 and SrBi4Ti4O15 ceramics have been prepared by the reactive-templated grain growth process. When slurries for tape casting are prepared using a solvent, binder, and plasticizer, large agglomerates are formed in the slurries by heterocoagulation between Bi2O3 and CaCO3 or SrCO3 particles. These agglomerates melt between 800° and 850°C, and the melt penetrates into surrounding powder layers, leaving large voids. Sintering at high temperatures cannot eliminate these voids, resulting in a low density. Furthermore, the voids disturb the alignment of platelike particles surrounding the voids. The use of dispersant in the preparation of the slurries suppresses the formation of the agglomerates, and dense, highly-textured materials are obtained.
- 社団法人粉体粉末冶金協会の論文
- 2008-04-15
著者
関連論文
- Hg1223における水銀サイトのカチオン部分置換が超伝導特性に与える影響
- ゾル-ゲル法により作製したLaNiO_3(100)/CeO_2(100)/Si(100)ヘテロ構造の構造解析
- アルコキシド及び水酸化物溶液を用いたゾル-ゲル法によるc軸配向NdBa_2Cu_3O_薄膜の作製
- ゾル-ゲル法によるAg添加NdBa_2Cu_3O_の合成と超伝導特性
- ゾル-ゲル法を利用したLaF_3薄膜の作製
- ゾル-ゲル法によるNdBa_2Cu_3O_超電導体の合成
- 普通焼結による配向性Bi_4Ti_3O_12セラミックスの作製(第2報) : 焼結機構
- 普通焼結による配向性Bi_3Ti_3O_12セラミックスの作製 : I. テープ成形と焼成
- ホットプレスしたチタン酸ビスマスセラミックスの粒子配向と電気的性質
- Bi_2O_3-TiO_2 混合物からの Bi_4Ti_3O_ の生成
- 反応性テンプレート粒成長法による配向性BaTiO_3バクルセラミックの製造
- Ag-マトリックス複合体の緻密化と微細構造変化に及ぼす第2相ZrO_2の影響
- 圧電セラミックスへの結晶配向技術の適用(周期空間と相互作用する新しいセラミックスのマテリアルデザインとプロセッシング)
- 低温相粉体を用いた緻密な圧電性PbNb_2O_6の作製
- BaTiO_3の焼結と微細構造に及ぼすLi_2Si_2O_5の影響
- ジルコン酸チタン酸鉛とガラスの化学反応に及ぼすガラス組成の影響(第2報) : ケイ酸鉛ガラスとホウケイ酸鉛ガラス
- ジルコン酸チタン酸鉛とガラスの化学反応に及ぼすガラス組成の影響(第1報) : ホウ酸鉛ガラス
- KSr_2Nb_5O_固溶体のキュリー温度に及ぼす粒子配向の影響
- RTGG法によるペロブスカイト型圧電セラミックスの配向制御に関する研究
- 亜鉛フェライト中の過剰の酸化鉄の挙動
- RTGG法による結晶配向性CaBi_4Ti_4O_およびSrBi_4Ti_4O_の作製におけるヘテロ凝集の影響
- 酢酸鉛とテトラエトキシシランから得られた複合アルコキシドの構造
- テンプレート粒成長法による圧電セラミックスの結晶配向プロセス (特集 先端セラミックスプロセス技術(1))