II族元素を添加したデラフォサイト型CuLaO_2の作製と発光特性
スポンサーリンク
概要
- 論文の詳細を見る
Single-phase delafossite-type CuMxLa1-xO2 (M=Mg, Ba, Ca, Sr, Mg, Zn, Cd) was synthesized by means of the solid-state reaction of a stoichiometrically mixed powder of binary oxides at 1273 K, for 10 h in an argon flow, and their luminescent properties were investigated. Undoped CuLaO2 exhibited a weak yellow-green photoluminescence-emission band due to the Cu+ interconfiguration transition at room temperature. The effect of II-group element doping on the photoluminescent properties was classified into two types. CuSrxLa1-xO2, CuBaxLa1-xO2 and CuZnxLa1-xO2 (x≤0.01) exhibited the emission slightly shifted to the shorter-wavelength side than that of undoped CuLaO2 and a strong emission intensity, with increasing doping concentration. These emission behaviors in CuSrxLa1-xO2, CuBaxLa1-xO2 and CuCaxLa1-xO2 was considered to be due to the formation of new emission centers upon doping Sr, Ba and Ca, respectively. CuZnxLa1-xO2, CuCdxLa1-xO2 and CuMgxLa1-xO2 (x≤0.01) exhibited the emission similar to one due to the Cu+ interconfiguration transition in undoped CuLaO2 and a weaker emission intensity, with increasing doping.
- 社団法人粉体粉末冶金協会の論文
- 2008-02-15
著者
-
勝井 明憲
東海大学開発工学部素材工学科
-
松下 裕亮
東海大学開発工学部素材工学科
-
松下 裕亮
東海大学開発工学部情報通信工学科
-
勝井 明憲
東海大学開発工学部物質化学科
-
高橋 祐介
東海大学開発工学部物質化学科
-
松下 裕亮
東海大学開発工学部
関連論文
- ゾルゲル合成CaMgSi_2O_6ゲルの結晶化に対する塩酸触媒の影響
- 生体活性ガラスセラミックス
- 三元カルコゲナイド化合物の結晶合成と電気的特性
- 開発工学部における「情報処理実習」に対する授業評価の要因分析
- 強磁性La_Sr_MnO_3セラミックのトンネル型磁気抵抗効果
- II族元素を添加したデラフォサイト型CuLaO_2の作製と発光特性
- (CuSb2O6)x(TiO2)1-x焼結体の作製と応用
- カルコパイライト形半導体の単結晶成長の為の生成過程解析
- アルカリ塩化物溶媒を用いたBi-Sr-Ca-Cu-Oの単結晶育成
- ゾルゲル法によるLi[x]CoO2の合成と評価
- ゾルゲル法により作製したCaMgSi2O6の結晶化過程
- (Zn,Mn)SnAs2磁性半導体の合成
- Ag-Sb-VI2系化合物(VI=Se, Te)の状態図と熱電特性
- 新入生を対象とした創成型科目"プレゼミナール"の試行
- 太陽電池用CuInS_2薄膜の作製と評価
- 示差熱分析による蛍光体材料IIaIII_2VI_4化合物の状態図作成と結晶成長
- 誘電体膜被覆によるたてカー効果のエンハンスメント
- CuInSe_2と薄膜型太陽電池への応用