Effects of Fast Reactor Irradiation Conditions on Tensile and Transient Burst Properties of Ferritic/Martensitic Steel Claddings

概要

論文の詳細を見る
The effects of fast neutron irradiation conditions have been investigated by focusing on the mechanical properties of 11Cr-0.5Mo-2W, Nb, V ferritic/martensitic (F/M) stainless steel (PNC-FMS) and 10.5Cr-1.5Mo, Nb, V F/M stainless steel (HT9M) claddings, especially tensile and transient burst properties. These two F/M claddings were irradiated at temperatures from 693 to 833 K to 42.5 dpa (displacement per atom) in the experimental fast reactor JOYO using the PFB090 fuel test subassembly. Post-irradiation tensile and temperature-transient-to-burst tests were carried out for defueled cladding specimens. The results of mechanical tests for the PNC-FMS cladding showed that there was no significant degradation in tensile and transient burst strengths even after fast neutron irradiation. On the other hand, the strength of the HT9M cladding tended to shift to lower values than those of as-received specimens. The differences in tensile and transient burst strengths between the two claddings were attributed to martensite structural stability which was related to the stable solid solution elements.
社団法人日本原子力学会の論文
2007-12-25