Suppression of the Formation of Large Pores in the Assimilated Parts of Sinter Produced Using Pisolitic Ores
スポンサーリンク
概要
- 論文の詳細を見る
Sintering experiments were carried out in order to suppress the formation of large pores existed in the assimilated parts of sinter produced using pisolitic ores. A briquette consisted of disk-shaped pisolitic ore specimen as core particle and fine mixture of hematite ore and limestone as shell layer was used for the experiments. CaO concentration of the shell layer was varied in two levels, <I>i.e., </I> 10 and 26 mass%. The influence of CaO concentration of the shell layer and heating rate on the performance of large pore formation during heating were examined by a microscopic observation. The mean diameter and the area fraction of pores existed in the assimilated part of specimen were also measured. The results obtained were as follows: By increasing CaO concentration of the shell layer from 10 to 26 mass%, the suppression of the large pore formation was achieved in terms of the decrease in both of the diameter and amount of pores. The amount of pores decreased with decrease in heating rate over the temperature of melt-formation for bath CaO concentration of the shell layer, but heating rate did not influence remarkably pore diameter. It is clear that the suppressible effect of the increase in CaO concentration of the shell layer on the formation of large pores is resulted from both of the promotion of coalescence of bubbles and decrease in the bubble size possible to move in the melt due to lowering apparent viscosity of the melt formed during heating.
- 社団法人 日本鉄鋼協会の論文
- 1996-11-15
著者
-
Kasai Eiki
Institute For Advanced Materials Processing Tohoku University
-
Otomo Takaho
Mining College Akita University
-
TAGUCHI Noboru
Mining College, Akita University
-
Kasai Eiki
Institute For Advance Materials Processing Tohoku University
-
Taguchi Noboru
Mining College Akita University
関連論文
- Vapor Pressure of Zinc and Zinc Chloride in the Fe_tO-CaO-SiO_2-Al_2O_3 Slag System
- Vaporization Behavior of Zinc from the FeO-CaO-SiO_2-Al_2O_3 Slag System
- Vapor Pressure Measurements for Metal Chloride Systems by the Knudsen Effusion Method
- Vapour Pressure Determination for PCDD/Fs by Knudsen Effusion Method
- Vapour Pressure Determination for Dibenzo-p-dioxin, Dibenzofuran, Octachlorodibenzo-p-dioxin and Octachlorodibenzofuran Using a Knudsen Effusion Method
- DIOXIN EMISSIONS IN RECYCLING PROCESSES OF METALS
- Measurement of Thermodynamic Functions of Solid Phase for DD, DF,OCDD and OCDF, and Estimation of Thermodynamic Functions of Gas Phase for PCDD/Fs Using Molecular Orbital Method with Density Functional Theory
- Determination of Vapor Pressures of PCDD/Fs by Kundsen Method
- Catalytic Performance of Several Metallic Oxides on The Elimination Reactions of NO
- Thermodynamic Analysis of Thermochemical Recovery of High Temperature Wastes
- Macroscopic Behaviors of Dioxins in the Iron Ore Sintering Plants
- Differential Thermal Analysis of Assimilation and Melt-formation Phenomena in the Sintering Process of Iron Ores
- Rate of Methane-steam Reforming Reaction on the Surface of Molten BF Slag-for Heat Racovery from Molten Slag by Using a Chemical Reaction-
- Reduction in Dioxin Emissions by the Addition of Urea as Aqueous Solution to High-temperature Combustion Gas
- Effect of Cr_2O_3 and WO_3 Addition on Pore Formation and Microstructure in Iron Foam
- Lowering Reduction Temperature of Iron Ore and Carbon Composite by Using Ores with High Combined Water Content
- Reduction Behavior of Hematite Composite Containing Polyethylene and Graphite with Different Structures with Increasing Temperature
- Feasibility of Rotary Cup Atomizer for Slag Granulation
- Effect of Raw Materials Bed Segregation on the Structural Change of Iron Ore Sintering Bed
- GRINDING OF EP DUST AND ITS EFFECT ON SOLUBILITY OF METAL COMPOUNDS IN WATER
- EFFECT OF DRY MIXED GRINDING OF TALC, KAOLINITE AND GIBBSITE ON PREPARATION OF CORDIERITE CERAMICS
- Observation of Behavior of Dioxins and Some Relating Elements in Iron Ore Sintering Bed by Quenching Pot Test
- A New Drying Process of Dusts and Sludge by Employing Heat Storage Materials
- Recent trends in the decomposition of chlorinated aromatic hydrocarbons by ultrasound irradiation and Fenton's reagent
- Effect of Additives on the Dioxins Emissions in the Iron Ore Sintering Process
- Carbothermic Reduction in the Combustion Bed Packed with Composite Pelles of Iron Oxide and Coal
- Suppression of the Formation of Large Pores in the Assimilated Parts of Sinter Produced Using Pisolitic Ores
- Formation of Dioxins and their Transfer in the Combustion Bed of Coke and Soil Containing PVC
- Remediation Technologies of Ash and Soil Contaminated by Dioxins and Relating Hazardous Compounds
- (1) REMOVAL OF IRON BEARING MINERALS FROM BAUXITE BY HIGH GRADIENT MAGNETIC SEPARATOR (One-day Symposium on Separation Technology) (Miscellany)
- Heat Transfer Analysis of the Mosaic Embedding Iron Ore Sintering (MEBIOS) Process
- Process Analysis of the Effective Utilization of Molten Slag Heat by Direct Blast Furnace Cement Production System
- Analysis of Granules Behavior in Continuous Drum Mixer by DEM
- Numerical Simulation Model for Granulation Kinetics of Iron Ores
- Effect of Chlorine on the Vaporization Behavior of Zinc and Lead during High Temperature Treatment of Dust and Fly Ash
- Utilization of Ores with High Combined Water Content for Ore–carbon Composite and Iron Coke
- Effect of Mixed-grinding on Reduction Process of Carbonaceous Material and Iron Oxide Composite
- Design of Bed Structure Aiming the Control of Void Structure Formed in the Sinter Cake
- Numerical Simulation Model of the Iron Ore Sintering Process Directly Describing the Agglomeration Phenomenon of Granules in the Packed Bed
- Modeling of Iron Ore Sintering Process by Combining Discrete Element Method and Gas-solid Heat Transfer Equiations
- Effect of Heat Wave Propagation on the Structural Changes in the Iron Ore Sintering Bed
- EFFECT OF MIXED DRINDING OF POWDERS ON SUPERCONDUCTING PROPERTIES OF YBa_2 Cu_3 O_ CERAMICS
- Effects of Slag Compositions on the Rate of Methane-Steam Reaction
- Theoretical Design of Cup Atomizer for Heat Recovery of Molten Slag by Chemical Quench
- Effect of Slag Basicity on the Rate of Methane-steam Reaction
- Essential Factors Governing Strength of Sintered Iron Ore Particles
- Reduction Mechanism of Iron Oxide-Carbon Composite with Polyethylene at Lower Temperature
- Preface to the Special Issue on "Recent Progress of the Research on the Iron Ore Agglomeration Process"
- Influence of Properties of Fluxing Materials on the Flow of Melt Formed in the Sintering Process
- EFFECT OF WATER CONTENT ON GRINDABILITY OF DOLOMITE AND ITS STRUCTURAL CHANGE
- Immersion treatment of sinter into calcium halide solution.