Thermodynamics of Molten Fe-Cr-C_<satd.> Alloy
スポンサーリンク
概要
- 論文の詳細を見る
The activity of chromium in molten Fe-Cr-C<SUB>satd.</SUB> alloy has been measured at temperatures ranging from 1548 to 1773 K by a chemical equilibrium technique. There is little temperature dependence of the activiy of chronium in the region of low chromium contents by weight, and the activity coefficient of chromium decreases as the chromium content increases.The activity coefficient of chromium in silver, which was needed for the foregoing measurement, was predetermined.By thermodynamic discussion in combination with the carbon solubility in molten iron-chromium alloys, the expression for the activity coefficient of chromium in Fe-Cr-C<SUB>satd.</SUB> alloy has been obtained as a function of chromium content and temperature as follows.ln<SUB>γ<SUB>Cr(s)</SUB></SUB>= -2.52+<SUB><I>T</I></SUB><SUP><U>3880</U></SUP> +(8.31-<SUB><I>T</I></SUB><SUP><U>23300</U></SUP>)<I>X</I><SUB>Cr</SUB>+(-4.21+<SUB><I>T</I></SUB><SUP><U>14900</U></SUP>)<I>X</I><SUB>Cr</SUB><SUP>2</SUP> (1623 to 1773K)The standard Gibbs energy of mixing of Fe-Cr-C<SUB>satd.</SUB> alloy was also estimated using the Gibbs-Duhem relationship, indicating that chromium and manganese behave similarly in terms of affinity for carbon and iron in molten carbon-saturated iron.
- 社団法人 日本鉄鋼協会の論文
- 1996-08-15
著者
-
Morita Kazuki
Department Of Biochemistry And Food Science Faculty Of Agriculture Kagawa University
-
Sano Nobuo
Department Of Metallurgy The University Of Tokyo
-
Sano Nobuo
Department Of Metallurgy Graduate School Of Engineering The University Of Tokyo
-
KOBAYASHI Yoshinao
The University of Tokyo
関連論文
- Thermodynamic Property of B in Molten Si and Phase Relations in the Si-Al-B System
- A Practical Method for Measuring Deoxynivalenol, Nivalenol, and T-2 + HT-2 Toxin in Foods by an Enzyme-linked Immunosorbent Assay Using Monoclonal Antibodies
- Interfacial Kinetics of Nitrogen with Molten Iron Containing Sulfur
- Dynamic Interfacial Phenomena between Gas, Liquid Iron and Solid CaO during Desulfurization
- Characterization of Fibrous Particles in Blast Furnace Slag Quenched by Water-spray
- Solubility of Chlorine in Aluminosilicate Slag Systems
- Activities of FeO in CaO-Al_2O_3-SiO_2-FeO and CaO-Al_2O_3-CaF_2-FeO Slags
- Measurement of Nitrogen Dissolution Rate into Molten Alloys by Isotope Exchange Technique (高温質量分析特集号)
- Effects of Oxygen and Nitrogen on the Rate of Nitrogen Dissolution in Iron-Chromium and Iron-Vanadium Alloys
- Chloride Capacities of CaO-SiO_2-Al_2O_3(-FeO, Mgo, MnO) Slags and Their Application in the Incineration Processes
- Activity Measurement of CaO-SiO_2-AlO_-MgO Slags Equilibrated with Molten Silicon Alloys
- A Newly Developed Method for Determining SiO_2 Activity of the Silicate Slags Equilibrated with Molten Silicon Alloys
- Thermodynamic Properties of Si-Al,-Ca, -Mg Binary and Si-Ca-Al, -Ti, -Fe Ternary Alloys
- Solubility of TiO_2 in Iron Saturated FeO-FeS Melts
- Resurrection of the iron and phosphorus resource in steel-making slag
- The Heating Characteristics of Cao-Sio_2-Fe_tO System Slags under Microwave Irradiation
- Thermodynamic Properties of the SiO_2-GeO_2 and Pt-rich Pt-Ge Systems at 1623 and 1723K
- Activity of AlO_ for the CaO-AlO_-CeO_ System at 1773K
- Carbothermic Reduction of MgO by Microwave Irradiation
- Solubility of TiO_2 in Fe_-FeS Melts
- Thermodynamics of the MnO-SiO_2-TiO_2 System at 1673 K
- Evaluation of Surface Tension and Adsorption for Liquid Fe-S Alloys
- Interfacial Phenomena Between Gas, Liquid Iron and Sold Lime During Desulfurization
- Determination of Macro-Contact Angle and Line Tension at High Temperatures for Au/Al_2O_3 System at 1373K Using a Micro-Scale Wetting Method
- Thermodynamics of the MnO-Al_2O_3-TiO_2 System
- Thermal Conductivity of the CaO-Al_2O_3-SiO_2 System
- Thermodynamics of Molten Fe-Cr-C_ Alloy
- 287 Phosphorus partitions between carbon-saturated iron melts and CaO-CaF_2-SiO_2-MnO slags(STEELMAKING, The 108th ISIJ Meeting)
- The Activity of Calcium in Calcium-Calcium Halide Fluxes
- Measurements of Thermodynamic Properties of Iron in Molten Silicon by Knudsen Effusion Method
- Refining of Si by the Solidification of Si-Al Melt with Electromagnetic Force
- The Distribution of Manganese and Sulfur between CaO Saturated CaO-FeO-SiO_2 Slags and Molten Iron
- Preface
- Determination of the Rate of CO_2 Dissociation on the Surface of CaO-SiO_ CaO-Al_2O_ CaO-SiO_2-CaF_2 and CaO-SiO_2-Fe_xO Melts
- Solubilities of Al2O3, SiO2 and Cr2O3 in the FeS Containing Systems
- The Solubility of MgO in Molten MgCl_2-CaCl_2 Salt
- Equilibrium Partitions of Manganese and Phosphorus between BaO-BaF2 Melts and Carbon Saturated Fe-Mn Melts.
- Phosphorus Partition between CaOsatd.-BaO-SiO2-FetO Slags and Liquid Iron at 1873K.
- Equilibrium Distribution Ratios of Phosphorus and Chromium between BaO-MnO Melts and Carbon Saturated Fe-Cr-Mn Alloys at 1 573 K.