A Newly Developed Method for Determining SiO_2 Activity of the Silicate Slags Equilibrated with Molten Silicon Alloys
スポンサーリンク
概要
- 論文の詳細を見る
- 2000-06-15
著者
-
MORITA Kazuki
Department of Materials Engineering, Graduate School of Engineering, The University of Tokyo
-
Morita Kazuki
Department Of Biochemistry And Food Science Faculty Of Agriculture Kagawa University
-
SANO Nobuo
Department of Metallurgy, The University of Tokyo
-
KUME Kousuke
Department of Metallurgy, The University of Tokyo
-
SANO Nobuo
Nippon Steel Corporation
-
Sano N
Nippon Steel Corporation
-
Sano Nobuo
Department Of Metallurgy Graduate School Of Engineering The University Of Tokyo
-
Kume Kousuke
Department Of Metallurgy The University Of Tokyo
-
Morita K
Department Of Metallurgy The University Of Tokyo
関連論文
- Thermodynamic Property of B in Molten Si and Phase Relations in the Si-Al-B System
- A Practical Method for Measuring Deoxynivalenol, Nivalenol, and T-2 + HT-2 Toxin in Foods by an Enzyme-linked Immunosorbent Assay Using Monoclonal Antibodies
- Interfacial Kinetics of Nitrogen with Molten Iron Containing Sulfur
- Dynamic Interfacial Phenomena between Gas, Liquid Iron and Solid CaO during Desulfurization
- Characterization of Fibrous Particles in Blast Furnace Slag Quenched by Water-spray
- Solubility of Chlorine in Aluminosilicate Slag Systems
- Activities of FeO in CaO-Al_2O_3-SiO_2-FeO and CaO-Al_2O_3-CaF_2-FeO Slags
- Measurement of Nitrogen Dissolution Rate into Molten Alloys by Isotope Exchange Technique (高温質量分析特集号)
- Effects of Oxygen and Nitrogen on the Rate of Nitrogen Dissolution in Iron-Chromium and Iron-Vanadium Alloys
- Chloride Capacities of CaO-SiO_2-Al_2O_3(-FeO, Mgo, MnO) Slags and Their Application in the Incineration Processes
- Activity Measurement of CaO-SiO_2-AlO_-MgO Slags Equilibrated with Molten Silicon Alloys
- A Newly Developed Method for Determining SiO_2 Activity of the Silicate Slags Equilibrated with Molten Silicon Alloys
- Thermodynamic Properties of Si-Al,-Ca, -Mg Binary and Si-Ca-Al, -Ti, -Fe Ternary Alloys
- Solubility of TiO_2 in Iron Saturated FeO-FeS Melts
- Resurrection of the iron and phosphorus resource in steel-making slag
- The Heating Characteristics of Cao-Sio_2-Fe_tO System Slags under Microwave Irradiation
- Thermodynamic Properties of the SiO_2-GeO_2 and Pt-rich Pt-Ge Systems at 1623 and 1723K
- Activity of AlO_ for the CaO-AlO_-CeO_ System at 1773K
- Carbothermic Reduction of MgO by Microwave Irradiation
- Solubility of TiO_2 in Fe_-FeS Melts
- Thermodynamics of the MnO-SiO_2-TiO_2 System at 1673 K
- Evaluation of Surface Tension and Adsorption for Liquid Fe-S Alloys
- Interfacial Phenomena Between Gas, Liquid Iron and Sold Lime During Desulfurization
- Determination of Macro-Contact Angle and Line Tension at High Temperatures for Au/Al_2O_3 System at 1373K Using a Micro-Scale Wetting Method
- Thermodynamics of the MnO-Al_2O_3-TiO_2 System
- Thermal Conductivity of the CaO-Al_2O_3-SiO_2 System
- Thermodynamics of Molten Fe-Cr-C_ Alloy
- 287 Phosphorus partitions between carbon-saturated iron melts and CaO-CaF_2-SiO_2-MnO slags(STEELMAKING, The 108th ISIJ Meeting)
- The Activity of Calcium in Calcium-Calcium Halide Fluxes
- Reply to Comments on "Evaluation of Thermodynamic Activity of a Metallic Oxide in a Ternary Slag from the Sulphide Capacity of the Slag"
- Measurements of Thermodynamic Properties of Iron in Molten Silicon by Knudsen Effusion Method
- Refining of Si by the Solidification of Si-Al Melt with Electromagnetic Force
- The Distribution of Manganese and Sulfur between CaO Saturated CaO-FeO-SiO_2 Slags and Molten Iron
- Preface
- Determination of the Rate of CO_2 Dissociation on the Surface of CaO-SiO_ CaO-Al_2O_ CaO-SiO_2-CaF_2 and CaO-SiO_2-Fe_xO Melts
- Solubilities of Al2O3, SiO2 and Cr2O3 in the FeS Containing Systems
- The Solubility of MgO in Molten MgCl_2-CaCl_2 Salt
- Equilibrium Partitions of Manganese and Phosphorus between BaO-BaF2 Melts and Carbon Saturated Fe-Mn Melts.
- Phosphorus Partition between CaOsatd.-BaO-SiO2-FetO Slags and Liquid Iron at 1873K.
- Equilibrium Distribution Ratios of Phosphorus and Chromium between BaO-MnO Melts and Carbon Saturated Fe-Cr-Mn Alloys at 1 573 K.