Thermal Conductivity of the CaO-Al_2O_3-SiO_2 System
スポンサーリンク
概要
- 論文の詳細を見る
Thermal conductivity of the CaO–Al2O3–SiO2 system, which is one of the most important silicate melts in iron- and steelmaking processes, was measured using non-stationary hot wire method in the range from liquidus temperature to 1 873 K. Measurements were carried out at various compositions, and iso-thermal conductivity line of the CaO–Al2O3–SiO2 system was drawn in iso-thermal sections at 1 673 K, 1 773 K, and 1 873 K. Thermal conductivity decreased with basicity increase, when CaO/SiO2 ratio is smaller than unity, whereas it showed constant value when CaO/SiO2 ratio is larger. In case Al2O3 content was varied at constant CaO/SiO2 ratio of 0.39 and 0.90, thermal conductivity showed maximum at 15–20 mass% Al2O3, suggesting that Al2O3 behaves as an amphoteric oxide. In the temperature range of interest, the thermal conductivity of each composition decreased as temperature rises. Temperature dependence showed deviation from linearity with the reciprocal of absolute temperature, which was considered to be due to the thermally-induced depolymerisation of the silicate structure at higher temperature. Also, thermal conductivity was found to conform to an exponential function of 1/T during deploymerization with the apparent activation energy.
- 社団法人 日本鉄鋼協会の論文
- 2006-03-15
著者
-
MORITA Kazuki
Department of Materials Engineering, Graduate School of Engineering, The University of Tokyo
-
Morita Kazuki
Inst. Of Industrial Sci. The Univ. Of Tokyo
-
Morita Kazuki
Department Of Biochemistry And Food Science Faculty Of Agriculture Kagawa University
-
KANG YoungJo
Department of Materials Science and Engineering, Royal Institute of Technology
-
Kang Youngjo
Inst. Of Industrial Sci. The Univ. Of Tokyo
-
Kang Youngjo
Department Of Materials Science And Engineering Royal Institute Of Technology
-
Morita Kazuki
Department Of Materials Engineering University Of Tokyo
-
KANG Youngjo
Department of Materials Engineering, University of Tokyo
関連論文
- Thermodynamic Property of B in Molten Si and Phase Relations in the Si-Al-B System
- A Practical Method for Measuring Deoxynivalenol, Nivalenol, and T-2 + HT-2 Toxin in Foods by an Enzyme-linked Immunosorbent Assay Using Monoclonal Antibodies
- Interfacial Kinetics of Nitrogen with Molten Iron Containing Sulfur
- Dynamic Interfacial Phenomena between Gas, Liquid Iron and Solid CaO during Desulfurization
- Characterization of Fibrous Particles in Blast Furnace Slag Quenched by Water-spray
- Solubility of Chlorine in Aluminosilicate Slag Systems
- Activities of FeO in CaO-Al_2O_3-SiO_2-FeO and CaO-Al_2O_3-CaF_2-FeO Slags
- Measurement of Nitrogen Dissolution Rate into Molten Alloys by Isotope Exchange Technique (高温質量分析特集号)
- Effects of Oxygen and Nitrogen on the Rate of Nitrogen Dissolution in Iron-Chromium and Iron-Vanadium Alloys
- Chloride Capacities of CaO-SiO_2-Al_2O_3(-FeO, Mgo, MnO) Slags and Their Application in the Incineration Processes