Properties of Core Ore in Quasi-particle Required for Large Amounts Usage of Limonitic Ores in Iron Ore Sintering Process
スポンサーリンク
概要
- 論文の詳細を見る
The fluidity of melt formed in the sintering process of iron ores is an important factor for producing a high-strength sinter. When using a large amount usage of limonitic ores as core ore of the quasi-particle of sinter mix, it is predicted that the fluidity of formed melt decreases, because the solid ratio in the melt increases by an acceleration of the assimilation of the core ore with the melt.In order to control the assimilation of limonitic ore, basic researches were conducted using a modeled briquette, which consisted of a disk-shaped iron ore core and a shell layer of fine mixture composed of Fe2O3 and CaCO3 reagents. Assimilation rate of various iron ores was measured, and then solid phase ratio in the melt was calculated based on the phase diagram of CaO-Fe2O3 system. According to the calculated solid phase ratio in the melt, the fluidity of melt was discussed. The results obtained are summarized as follows:Fair linear relations were obtained between the porosity of core ore after dehydration and the combined water content of the ore. The assimilation rate of core ore at a specified temperature was represented as a function of the porosity of core ore after dehydration and the holding time at the temperature. The diameter and the apparent density of core ore influenced the calculated solid phase ratio in the melt. It was suggested that an optimal sinter structure was achieved by mixing a large and dense core ore at about 20 mass% in raw mix.
- 社団法人 日本鉄鋼協会の論文
- 2005-04-15
著者
-
Takasaki Yasushi
Fac. Of Engineering And Resource Sci. Akita Univ.
-
Takasaki Yasushi
Faculty Of Engineering And Resource Science Akita University
-
OTOMO Takaho
Faculty of Engineering and Resource Science, Akita University
-
KAWAGUCHI Takazo
Corporate Research & Development Laboratories, Sumitomo Metal Industries, Ltd.
-
Otomo Takaho
Fac. Of Engineering And Resource Sci. Akita Univ.
-
Otomo Takaho
Faculty Of Engineering And Resource Science Akita University
-
Kawaguchi Takazo
Corporate Research & Development Laboratories Sumitomo Metal Industries Ltd.
-
Kawaguchi Takazo
Corporate R&d Laboratories Sumitomo Metal Industries Ltd.
関連論文
- Analysis of Raw Material Flow with Axial Direction in Continuous Drum Mixer for Sintering Process
- Granule Design for the Sintering with Less Amount of Liquid Phase Formation
- Properties of Core Ore in Quasi-particle Required for Large Amounts Usage of Limonitic Ores in Iron Ore Sintering Process
- Copper Leaching Behavior of Iron-Oxide Hosted Copper-Gold Ore in Sulfuric Acid Medium
- Carbothermic Reduction in the Combustion Bed Packed with Composite Pelles of Iron Oxide and Coal
- Analysis of Granules Behavior in Continuous Drum Mixer by DEM
- Numerical Simulation Model for Granulation Kinetics of Iron Ores
- Development of a 3-D Sinter Process Mathematical Simulation Model
- Influence of Properties of Fluxing Materials on the Flow of Melt Formed in the Sintering Process
- Improvement of Sinter Softening Property and Reducibility by Controlling Chemical Compositions
- Production of Carbon Included Sinter and Evaluation of Its Reactivity in a Blast Furnace Environment
- Sintering Behavior of Raw Material Bed Placing Large Particles
- Summarized Achievements of the Porous Meso-mosaic Texture Sinter Research Project
- Recovery of Pt and Pd from PGM Mine Tailings by Magnetic Separation
- Comparative Study of Metals Recovery Process from Effluent Water of a Metallurgical Refining Process
- Improvement of Sinter Productivity by Adding Return Fine on Raw Materials after Granulation Stage