焼鈍マルテンサイト組織を母相とする高強度低合金TRIP鋼板の伸びフランジ性と曲げ性に及ぼす熱処理条件の影響

概要

論文の詳細を見る
The effects of heat-treatment conditions on stretch-flangeability and bendability of 800 MPa grade 0.2C-1.5Si-1.5Mn low alloy TRIP-aided sheet steels with annealed martensitic matrix or "TRIP-aided annealed martensite steels" were investigated for automotive applications. Good stretch-flangeability and excellent bendability, as well as large ductility, were achieved in the steels intercritically annealed at 780-820℃, followed by austempering at 375-400℃ for 100-1000 s. In this case, initial microstructure prior to intercritical annealing was martenite or fine bamite structure transformed at temperatures below 400℃. These good formabilities were considered to be caused by fine annealed lath matnx with low dislocation density, interlath stable retained austenites and relatively low difference in strength between second phase and matnx.