Transparent pyrex glasses were obtained by sintering a green compact, which was fabricated by using CIP method for pyrex glass powder, in diverse atmosphere (air, Ar, He and vacuum (10-2Pa)) at 973-1173K. Effects of sintering conditions (temperature and atmosphere) on transmittance of sintered glasses were investigated. Devitrification resulting from crystallization of cristobalite arose in all atmosphere at temperatures over 1023K. Optimum sintering condition for fabricating transparent sintered pyrex glass was at 1003 K for 1hour in a vacuum (10-2 Pa) or He atmosphere in this work. The transparency was 15∼20% in visible region and was about 60% in infrared region. The relationship between transparency and condition of the sintered glasses was discussed in terms of permeation constant of gas species during sintering.
- 社団法人 資源・素材学会の論文
- 2004-08-25
著者
-
藤野 茂
九州大学大学院総合理工学研究院 融合創造理工学部門
-
藤野 茂
九州大学大学院工学研究院化学工学部門
-
藤野 茂
九大
-
吉田 慎
九州大学大学院総合理工学府 量子プロセス理工学専攻 修士課程
-
森永 健次
九州大学大学院総合理工学研究院 融合創造理工学部門
-
森永 健次
九州大学大学院総合理工学研究科
-
MORINAGA Kenji
九州大学大学院総合理工学研究科材料開発工学専攻
-
藤野 茂
九州大学大学院 工学研究院 化学工学部門
関連論文
- 21pTJ-9 高速点火核融合実験用散乱中性子計測器の開発(21pTJ 核融合プラズマ(慣性),領域2(プラズマ基礎・プラズマ科学・核融合プラズマ・プラズマ宇宙物理))
- シレナイト系単結晶育成のためのT-T-T図とC-C-T図
- 超音波パルス法を用いた酸化物ガラスのデバイ温度と比熱の関係(物性,一般)
- 27pYL-8 レーザー核融合燃料面密度計測のための高速応答リチウム6シンチレーター(核融合プラズマ(慣性)(輸送/不安定性/他),領域2,プラズマ基礎・プラズマ科学・核融合プラズマ・プラズマ宇宙物理)
- 透明パイレックスガラス作製のための焼結温度ならびに雰囲気の影響
- Ba0-Zn0-P_20_5ガラス融体の密度, 表面張力, 粘度
- SrO-ZnO-P_2O_5ガラス-Al_2O_3複合材の作製とその特性
- 多成分ガラスの光物性と光ファイバー応用
- レーザー材料として見たフッ化物ガラス : 真空紫外領域における透過率, 屈折率
- 高温領域におけるガラスの表面張力の評価技術 (特集 ガラスの高温特性)