FeO_X-SiO_2基スラグと各種のCu_2S-Ni_3S_2-FeS系マット間の1,573Kにおける相平衡について
スポンサーリンク
概要
- 論文の詳細を見る
As a fundamental study for systematic and comprehensive understanding of copper and nickel smelting processes from a standpoint of thermodynamics, the phase equilibrium between the FeOX-SiO2 base slag, which was saturated with silica and containing about 6 mass % MgO, and the Cu2S-Ni3S2-FeS matte with NNi /(NNi + NCu) molar ratios of 0, 0.25, 0.5, 0.75 and 1 was investigated at 1,573 K under the partial pressure of SO2 with 0.1 atm. The slag and the matte were equilibrated in a MgO crucible and the partial pressures of oxygen and sulfur were controlled by using an Ar-SO2-S2 gas mixture passing through a sulfur reservoir. It was clarified that the partial pressures of oxygen and sulfur in relation to the iron content in the matte were almost independent of the matte species. This was considered to be ascribed to the activity of FeS in the matte which was almost constant against the matte species when the composition of iron in the matte was specified. The content of copper in the slag at a specified composition of iron in the matte decreased with increasing the nickel molar ratio, NNi /(NNi + NCu), in the matte while that of nickel increased with increasing the nickel molar ratio. It was found that the distribution ratio of silver between the slag and matte phases was considerably small at less than 0.1 and had a tendency to increase with increasing the nickel molar ratio in the matte when the composition of iron in the matte was specified. On the other hand, the distribution ratio of cobalt presented considerably large values of about 1 in the range of low iron content in the matte.
- 社団法人 資源・素材学会の論文
著者
-
日野 光久
東北大学 多元物質科学研究所
-
板垣 乙未生
東北大学素材工学研究所
-
板垣 乙未生
東北大 ・ 素材研
-
Font J
東北大 素材工研
-
Itagaki Kimio
Institute For Advanced Materials Processing Tohoku Univ
-
Hino Mitsuhisa
Institute Of Multidisciplinary Research For Advanced Materials Tohoku University
-
日野 光久
東北大学素材工学研究所
-
日野 光久
東北大・素材研
-
FONT Jonkion
東北大学素材工学研究所
関連論文
- Cu-Fe-As3 元系スパイスとスラグ間の平衡について
- 溶融CaO-SiO_2-FeO_系スラグ中のアンチモン,ヒ素の流動法による揮発度および蒸気圧測定
- 低酸素分圧下で酸化した Nb および Y 被覆 TiAl の酸化被膜
- K-2322 強磁性形状記憶合金Ni_2MnGaスパッタ膜の機械的特性(J03-4 知的複合材料)(J03 知的材料・構造システム)
- K-0404 強磁性形状記憶合金Ni_2MnGa膜の形状記憶特性(S08-1 機能特性・変態)(S08 形状記憶合金の製造・加工技術と機能発現)
- 強磁性形状記憶合金Ni_2MnGaの特性
- 気相制御研究分野 (2000.1-2000.12)(研究活動報告)
- ナノインデンテーション法による LaNi_5 スパッタ薄膜の機械的特性の評価
- 327 強磁性形状記憶合金Ni_2MnGa薄膜の作製と評価(OS 多機能・複合機能化への材料協調設計)
- 318 Ni_2MnGa スパッタ膜の形状記憶効果
- 還元拡散法による希土類-ニッケル系水素吸蔵合金粉末の直接製造 (特集 金属素材プロセス次世代への展望) -- (ニオブ・タンタル・希土類金属)
- 気相制御研究分野 (1999.1-1999.12) (研究活動報告)
- 気相制御研究分野 (1997.1-1997.12)(研究活動報告)
- 気相制御研究分野 (1998.1-1998.12) (研究活動報告)
- Zr-Ni-Mn3元系合金の組織と水素吸蔵特性
- 気相制御研究分野 (1996. 1-1996. 12) (研究活動報告)
- スパッタリング法によるLaNi_5水素吸蔵合金薄膜の作製およびその評価
- 気相制御研究分野 (1995. 1-1995. 12)(研究活動報告)
- 技術部 (1996. 1-1996. 12) (研究活動報告)
- 技術部 (1995. 1-1995. 12)(研究活動報告)
- ベースメタル研究ステーション (2000.1-2000.12)(研究活動報告)
- 溶融Cu_2S-Sb_2S_3およびFeS-Sb_2S_3系の熱力学的研究
- Cu_2S-FeS-Sb_2S_3系の熱力学的研究
- カルシウム熱還元法により作製された Ti-Ni 合金粉末の特性
- Silver Activity in Cu-Fe-S Matte Saturated with Copper Alloy
- Activity of Silver in Molten Copper Sulfide Saturated with Copper
- Activities of Se and Te in Molten Copper Sulfide Coexisting with Copper
- LaNi_5 水素吸蔵合金の薄膜作製に関する最近の研究
- ベースメタル研究ステーション (1996. 1-1996. 12) (研究活動報告)
- ベースメタル研究ステーション (1995. 1-1995. 12)(研究活動報告)
- ベースメタル研究ステーション (1997.1-1997.12)(研究活動報告)
- ベースメタル研究ステーション (1998.1-1998.12) (研究活動報告)
- 熱量測定によるCd-Te系融体の熱力学的研究
- 流動法によるPb-FeO_-CaO-SiO_2系およびPbO-ZnO-FeO_2系スラグ融体中のPbOの蒸気圧測定
- QSL法に関連する鉛含有スラグの均一融体組成域について
- 堅型流動法による溶融スラグ中の酸化鉛の蒸気圧測定
- 金属鉛と平衡する各種のPbO基スラグの均一融体領域について
- 金属鉛とPbO-FeO_x-CaO-SiO_2系ないしはPbO-FeO_x-CaO-SiO_2-ZnO系スラグ間の微量成分の分配挙動
- QSL鉛製錬法の化学熱力学的考察
- 金属鉛とPbO-FeO_x-CaO-SiO_2系ないしはPbO-FeO_x-CaO-SiO_2-ZnO系スラグ間の1,423Kにおける相平衡
- ベースメタル研究ステーション (1999.1-1999.12) (研究活動報告)
- Phase Equilibrium between FeO_x-SiO_2 Base Slag and Cu_2S-Ni_3S_2-FeS Mattes with Different Cu and Ni Contents at 1573K
- Phase Equilibrium and Minor Elements Distribution between Iron-Silicate Base Slag and Nickel-Copper-Iron Matte at 1573K under High Partial Pressures of SO_2
- THERMODYNAMIC EVALUATION OF DISTRIBUTION BEHAVIOR OF VA ELEMENTS IN NICKEL MATTE SMELTING
- Minor Elements Distribution between Iron-Silicate Base Slag and Ni_3S_2-FeS Matte under High Partial Pressures of SO_2
- 金属カルシウムを用いた鉄基合金からのニッケル, コバルトの分離
- 溶融錫を溶媒として用いたステンレス鋼中のニッケル, コバルトの分離
- 2. 熱量測定による溶融III-V族合金の熱力学諸量の導出
- III-V 族合金の平衡蒸気圧と化合物半導体の気相制御
- 非鉄製錬ダスト生成に関する熱力学
- Phase Relations, Activities and Minor Elements Distribution in Fe-Pb-As and Fe-Pb-Sb Systems Saturated with Carbon at 1473K
- Fe-Co-AsおよびFe-Co-Sb合金の1150℃における相関係と成分活量
- Phase Relations and Activities in the Fe-Ni-As and Fe-Ni-Sb Systems at 1423K
- Phase Relations and Activities in the Fe-Ni-As and Fe-Ni-Sb Systems at 1423K
- Phase Equilibrium between Ni-S Melt and CaO-Al_2O_3 Based Slag in CO-CO_2-SO_2 Gas Mixtures at 1773K
- Phase Equilibrium between Ni-S Melt and FeO_x-SiO_2 or FeO_x-CaO Based Slag under Controlled Partial Pressures
- Phase Equilibrium between Ni-S Melt and Slags under Controlled Partial Pressure of SO_2
- Distribution of Ni, Cr, Mn, Co and Cu between Fe-Ni Alloy and FeO_x-MgO-SiO_2 Base Slags
- 溶融スラグ中のヒ素およびアンチモンの揮発特性
- FeO_x-MgO-SiO_2 系スラグとニッケル合金間のCr, Cuの分配に及ぼすAl_2O_3, CaOの影響
- Cu-Feマットと銅の2液相分離範囲における銀の活量
- FeO_X-SiO_2基スラグと各種のCu_2S-Ni_3S_2-FeS系マット間の1,573Kにおける相平衡について
- ニッケル合金とFeO_X-MgO-SiO_2スラグ間のクロムの分配
- Phase Relation and Activity of Antimony in Cu-Fe-S-Sb System at 1473K
- Activity Measurements of Arsenic and Antimony in Miscibility Gap of Liquid Cu-O System
- Phase Relations and Activity of Arsenic in Cu-Fe-S-As System at 1473 K
- Phase Equilibria of Two-liquid CaO-MgO-Fe_tO-P_2O_5 Slag Saturated with (Mg, Fe)O
- Elution Mechanism of Fluorine form Steelmaking Slag into Seawater
- Dissolution Behavior of Environmentally Regulated Elements from Steelmaking Slag into Seawater
- Dissolution Behavior of Nutrition Elements from Steelmaking Slag into Seawater
- Dissolution behavior of environmentally regulated elements from steelmaking slag into seawater
- Dissolution behavior of nutrition elements from steelmaking slag into seawater
- Activity Measurement of the Constituents in Molten Sn-Mg-Zn-Ternary Lead Free Solder Alloys by Mass Spectrometry
- Activity Measurement of Silicon in Molten Cu-Si Binary Alloy
- マグネシウム及びリチウム熱還元法によるニッケルーミッシュメタル合金の直接製造に関する研究
- Identification of Titanium Oxide Phases Equilibrated with Liquid Fe-Ti Alloy Based on EBSD Analysis
- Carburization Degree of Iron Nugget Produced by Rapid Heating of Powdery Iron, Iron Oxide in Slag and Carbon Mixture
- Temperature Dependence of Ti Deoxidation Equilibria of Liquid Iron in Coexistence with 'Ti_3O_5' and Ti_2O_3
- Behavior of Ironmaking Slag Permeation to Carbonaceous Material Layer
- Equilibrium between Titanium and Oxygen in Liquid Fe-Ti Alloy Coexisted with Titanium Oxides at 1873K
- Kinetic Analysis of Iron Carburizaiton during Smelting Reduciton
- SOLUBILITY OF COPPER OR NICKEL IN IRON-SILICATE BASE SLAG EQUILIBRATED WITH Cu_2S-FeS OR Ni_3S_2-FeS MATTE UNDER HIGH PARTIAL PRESSURES OF SO_2
- ニッケル合金とFeO_x-MgO-SiO_2系ないしはFeO_x-CaO-MgO-SiO_2系スラグ間の相平衡
- FeO_X-MgO-SiO_2系スラグへのニッケルおよび銅の溶解
- 銅合金と平衡するCu-Fe-Sマット中のテルルの活量
- はんだ用共晶合金の熱含量測定
- 銅溶錬におけるマットの役割 (特集 硫化物の物性と製造プロセス)
- 銅およびニッケルマットの酸素富化溶錬に関する熱力学的研究
- 銅の溶錬プロセスにおける砒素の挙動
- Distribution of Minor Elements between MgO Saturated FeO_x-MgO-SiO_2 or FeO_x-CaO-MgO-SiO_2 Slag and Nickel Alloy
- 2) 非鉄金属溶錬におけるマットの役割(主題 : 硫化物の素材プロセッシングと機能)(特定テーマシンポジウム)(素材工学研究会記事)
- スパイスの生成と相平衡
- Cu-Zn-S系,Cu-Zn-Fe-S系およびCu-Zn-Pb-S系の1,473Kにおける相関係
- 溶融Cu-Zn-Fe系合金の亜鉛の活量
- Phase Equilibrium and Minor Elements Distribution between SiO_2-CaO-FeO_x-MgO Slag and Copper Matte at 1573K under High Partial Pressures of SO_2
- DISSOLUTION OF NICKEL AND COPPER IN FeO_x-SiO_2-MgO SLAG EQUILIBRATED WITH Nickel ALLOY
- (7) 質量分析計を用いるマット中微量元素の熱力学的研究(主題 : ベースメタル製錬の新しい展開)(平成 10 年度ベースメタル研究ステーションシンポジウム)(素材工学研究会記事)
- (3) 高 P_ 雰囲気での銅製錬(主題 : 鉄鋼・非鉄金属の製・精錬と凝固・鋳造のフロンティア)(第 2 回ベースメタル研究ステーションセミナー)(素材工学研究会記事)
- 金属のリサイクリングにおける熱力学
- 金属熱還元法における RNi_5 (R : La, Ce, Pr) 生成反応の熱収支について