Photoacoustic and Photoluminescence Characterization of Passivated and Unpassivated Mn-Doped ZnS Nanoparticles
スポンサーリンク
概要
- 論文の詳細を見る
In this study, passivated and unpassivated nanocrystalline ZnS with varying Mn2+ concentrations (ZnS:Mn) were synthesized and their photoacoustic (PA) and photoluminescence (PL) characteristics were studied. The PA intensity peak for the nanocrystalline ZnS was found to be blue-shifted compared with that for the bulk material due to quantum confinement effects. The difference of the PA signals of doped ZnS and undoped ZnS yielded the Mn2+ optical absorption spectra. The intensity of the PA peak increased linearly with Mn concentration. The PL spectra showed a peak position at 2.08 eV corresponding to the $d$–$d$ transition of Mn2+. For the unpassivated sample, a decrease in the PL intensities for higher Mn concentrations was observed. This could be attributed to concentration quenching. Addition of acrylic acid as a passivator led to an increase in PL intensity for all Mn concentrations and prevented the decrease in the PL intensity for higher Mn concentrations. These could be attributed to the surface passivation, which reduces the nonradiative recombination probabilities, thus increasing PL intensities.
- Published by the Japan Society of Applied Physics through the Institute of Pure and Applied Physicsの論文
- 2005-06-15
著者
-
Shen Qing
Department Of Applied Chemistry Faculty Of Engineering University Of Tokyo
-
Toyoda Taro
Department Of Applied Physics And Chemistry The University Of Electro-communications
-
Cruz Almira
Department Of Applied Physics And Chemistry And Course Of Coherent Optical Science The University Of
-
Shen Qing
Department of Applied Physics and Chemistry, and Course of Coherent Optical Science, The University of Electro-Communications, 1-5-1 Chofugaoka, Chofu, Tokyo 182-8585, Japan
-
Toyoda Taro
Department of Applied Physics and Chemistry, and Course of Coherent Optical Science, The University of Electro-Communications, 1-5-1 Chofugaoka, Chofu, Tokyo 182-8585, Japan
-
Cruz Almira
Department of Applied Physics and Chemistry, and Course of Coherent Optical Science, The University of Electro-Communications, 1-5-1 Chofugaoka, Chofu, Tokyo 182-8585, Japan
関連論文
- 27pYD-2 1T-TaS_2の価電子帯及び内殻光電子スペクトルの温度依存性(電荷密度波)(領域6)
- 28pPSA-1 CdSe量子ドット増感太陽電池電極の電子構造の硬XPS研究II(28pPSA 領域5ポスターセッション,領域5(光物性))
- 22pPSA-5 Sb吸着Si(111)表面のスピン分解ARPES(22pPSA 領域9ポスターセッション,領域9(表面・界面,結晶成長))
- 22aXA-4 V族(111)表面におけるスピン分裂バンドの直接観測(22aXA 表面界面電子物性,領域9(表面・界面,結晶成長))
- 22aPS-17 CdSe量子ドット増感太陽電池電極の電子構造の硬X線光電子分光研究(22aPS 領域5ポスターセッション,領域5(光物性))
- 23pPSA-15 CdSe量子ドットを吸着したナノ構造TiO_2電極の硬X線光電子分光(領域5ポスターセッション,領域5,光物性)
- 19pTB-13 ホイスラー型合金Ru_Fe_xCrGeの電子状態(19pTB f電子系・化合物磁性,領域3(磁性,磁気共鳴))
- 2P2-20 光音響法のナノ構造酸化チタン薄膜の熱拡散率評価への応用(ポスターセッション)
- 30pYB-10 Si(111)再構成表面上のAlナノクラスターの局所電子状態の研究(30pYB 表面界面電子物性,領域9(表面・界面,結晶成長))
- 18pTG-1 ビスマス表面状態のスピン角度分解光電子分光(表面界面電子物性,領域9,表面・界面,結晶成長)
- 20aYD-6 Bi(111)単結品表面のスビン分裂電子状態(20aYD 放射光・光電子(表面・薄膜・低次元物質),領域5(光物性))
- 26pTD-2 Bi(111)単結晶表面のスピン角度分解光電子分光(表面界面電子物性,領域9,表面・界面,結晶成長)
- 24aTK-3 スピン分解光電子分光を用いたfcc Co表面バンド構造の観測(光電子分光・MCD,領域5,光物性)
- 18aTB-5 Fe/Co超薄膜のスピン偏極バンド構造の観測(18aTB 領域3,領域9合同 2.表面・界面磁性,領域3(磁性,磁気共鳴))
- 24pQE-11 Fe/Co(001)のスピン偏極バンド構造(24pQE 軟X線発光・散乱・放射光真空紫外分光・MCD・光電子分光,領域5(光物性))
- 27aSC-6 fcc Co/Cu(001)超薄膜のスピン偏極表面電子状態(27aSC 薄膜・人工格子磁性,表面・界面磁性,領域3(磁性,磁気共鳴))
- ナノ結晶Si表面に吸着したCdSe量子ドットによる熱拡散率変化
- 1-04P-16 結晶型の異なるナノ構造TiO_2電極における光音響スペクトルと過渡電流特性(ポスターセッション 1)
- 近接場ヘテロダイン過渡格子法による酸化チタンナノ粒子薄膜の熱拡散率評価
- 量子ドット増感太陽電池の開発動向 (特集 太陽光発電技術の最新動向)
- 光-超音波-音響 ナノ構造TiO2電極に吸着したAu量子ドットの光音響スペクトル
- 1J1-2 光音響分光法によるCdSe量子ドットを吸着したナノ結晶Siの熱拡散率評価(超音波物性・材料・フォノン物理)
- 光音響分光法によるCdSe量子ドットを吸着したナノ結晶Siの熱拡散率評価
- ナノ構造TiO_2電極に吸着したAu量子ドットの光音響スペクトルと過渡応答評価
- 陽極化成法により作製したTiO_2ナノチューブ電極の光音響スペクトルと光電気化学特性
- 光音響分光法によるCdSe量子ドットを吸着したポーラスシリコンの熱物性評価(非線形音響,一般)
- 26aPS-5 CdSe量子ドットを吸着したナノ構造TiO_2電極の硬X線光電子分光II(ポスターセッション,領域5,光物性)
- 1-04P-18 TiO_2ナノチューブ電極に吸着したCdSe量子ドットの光音響スペクトルと光励起キャリアダイナミクス(ポスターセッション 1)
- 1-04P-17 CdS量子ドットを吸着したナノ構造TiO_2電極の光音響スペクトルと過渡応答特性(ポスターセッション 1)
- 1-04P-15 ナノ構造TiO_2膜に吸着したAu量子ドットの光音響スペクトル(ポスターセッション 1)
- 1-04-03 光音響法によるナノ結晶Si膜の熱物性評価(光-超音波エレクトロニクス)
- CdSe量子ドットを吸着したTiO_2ナノチューブ電極の光音響スペクトルと光電流特性(非線形・一般)
- 29pRE-6 Co/Cu(001)超薄膜のスピン角度分解MDAD効果(29pRE 光電子分光・逆光電子分光,放射光真空紫外分光,軟X線発光,領域5(光物性))
- 28aPS-12 fcc Co/Cu(001)のスピン角度分解光電子分光スペクトルの膜厚依存性(28aPS 領域5ポスターセッション,領域5(光物性))
- Dependence of the X-Ray Photoacoustic Signal Intensity of Pure Copper and Brass on Sample Thickness
- Dependence of the X-Ray Photoacoustic Signal Intensity of Brass on Sample Thickness and Modulation Frequency
- Hard X-Ray Absorption Spectroscopy of Copper Alloys and Compounds with a Photoacoustic Detector : Photoacoustic Effect and Spectroscopy
- X-ray Absorption Near Edge Structure (XANES) of CuInSe_2, Brass and Phosphor Bronze by Photoacoustic Method : Photoacoustic Spectroscopy
- X-Ray Photoacoustic Spectroscopy of Brass
- Photoacoustic Response to X-Ray Absorption in Copper and Brass
- J-2 CdSe量子ドットを吸着したTiO_2ナノチューブ・ナノワイヤー複合電極の光音響評価と光電気化学特性(光-超音波・光音響法)
- 1Pa-5 陽極化成法による自己組織化TiO_2ナノチューブ電極の光音響スペクトル(ポスターセッション)
- 1Pa-7 多孔質ZnO薄膜の光音響分光特性(ポスターセッション)
- Analysis of Metallic Multilayers Using Hypersonic Surface Waves Induced by Transient Reflecting Gratings
- P3-59 透明電極FTOとナノ構造SnO_2電極に吸着したCdSe量子ドットの光音響スペクトルと光電気化学特性(ポスターセッション3(概要講演))
- 1Pa-6 PbS量子ドットを吸着したナノ構造TiO_2電極の光音響・光電気化学特性(ポスターセッション)
- 24aPS-123 低温STMとPES複合装置によるAl/Si(111)表面構造と電子状態の観察(表面・界面, 結晶成長,領域9(表面・界面, 結晶成長))
- 透過型光音響法によるポーラスシリコン膜の熱物性評価
- PHOTOACOUSTIC AND REFLECTION SPECTRA OF TiO_2 INVERSE OPAL ELECTRODES ADSORBED WITH CdSe QUANTUM DOTS
- 物性評価 CdSe量子ドットを吸着したフォトニックTiO2電極の光音響スペクトルと光電変換特性
- Photoacoustic and Photoelectrochemical Characterization of Inverse Opal TiO_2 Sensitized with CdSe Quantum Dots
- CdSe量子ドットを吸着したフォトニックTiO_2電極の光音響スペクトルと光電変換特性(非線形音響/一般)
- P3-66 CdSe量子ドットを吸着したTiO_2フォトニック結晶電極の光音響スペクトルと光電気化学特性(ポスターセッション3(概要講演))
- Photoacoustic and Photoelectrochemical Characterization of CdSe Quantum Dots Grafted onto Fluorine-Doped Tin Oxide (FTO) Substrate
- 物性評価 光音響法と光化学電流法によるCdSe量子ドットを吸着したナノチューブ・ナノワイヤTiO2電極の評価
- 物性評価 光音響法と光電気化学電流法によるCdSe量子ドットを吸着したナノ構造TiO2電極の評価
- P1-48 透明電極FTOに吸着したCdSe量子ドットの光音響法と光電気化学電流法による評価(ポスターセッション1(概要講演))
- P1-47 光音響法と光化学電流法によるCdSe量子ドットを吸着したナノ粒子混合系TiO_2電極の評価(ポスターセッション1(概要講演))
- P2-E-35 光音響法と光電気化学電流法による、CdSe量子ドットを吸着したナノ構造TiO_2電極の評価(光-超音波・光音響法,ポスターセッション2(概要講演))
- Evaluation of ZnO Varistors by Photoacoustic Spectroscopy
- X-Ray Photoacoustic Spectroscopy of ZnO Thin Film
- Theory of Transient Reflecting Grating in Fluid/Metallic Thin Film/Substrate Systems for Thin Film Characterization and Electrochemical Investigation
- Laser-Stimulated Scattering Microscope Study of an Jon-Implanted Silicon Surface
- Green Emission in CdS Films Deposited on CdInGaS_4 by Evaporation Method
- Optical Properties of Zn_xCd_InGaS_4 System
- Photothermal Effect in Compound Semiconductors CdInGaS_4 and CdIn_2S_4
- Hydrostatic Pressure Dependence of the Fundamental Absorption Edges of CdInGaS_4 and ZnIn_2S_4
- スパッタ法で作製したTiO_2電極の光音響スペクトルと光電気化学特性 : 酸素分圧特性(一般及び非線形音響)
- Dependence of the Photoacoustic Signal Intensity on Modulation Frequency for CdInGaS_4 Crystals under a Transmission Detection Configuration
- Photoacoustic Characterization of Thermal and Electronic Transport Properties of CdInGaS_4 in a Transmission Detection Configuration
- Photoacoustic and Photoluminescence Studies of CdS_xSe_ Doped Glasses
- TiO_2電極における電圧印加処理効果が光音響スペクトルに及ぼす効果
- Characterization of Electronic States of TiO_2 Powders by Photoacoustic Spectroscopy
- P2-E-36 粒径の異なるナノ粒子混合系を用いたTiO_2電極の光音響スペクトルと光電気化学特性(光-超音波・光音響法,ポスターセッション2(概要講演))
- 陽極化成法による自己組織化TiO_2ナノチューブ電極の光音響スペクトル(非線形音響,一般)
- Photoacoustic Spectra of Mixed TiO_2 Ultrafine Powders with Rutile and Anatase Structures
- Photoacoustic and Photoluminescence Spectra of ZnS:Mn Nanocrystals
- Screen-printed Cu_2S-based Counter Electrode for Quantum-dot-sensitized Solar Cell
- Electric Characteristics of Li2O-Doped TiO2 Nanocrystalline Film and Its Application to Dye-Sensitized Solar Cells
- P3-54 光音響法とフォトルミネッセンス法によるナノ結晶Siの評価 : 陽極化成時のHF濃度依存性(ポスターセッション3(概要講演))
- 光音響法によるナノ結晶Siの評価(一般及び非線形音響)
- P1-49 光音響法と光化学電流法によるナノ構造TiO_2電極の評価 : アニール温度依存性(ポスターセッション1(概要講演))
- P1-46 ナノ結晶シリコンの光吸収・熱物性の評価(ポスターセッション1(概要講演))
- Room-Temperature Absorption Edge of InGaN/GaN Quantum Wells Characterized by Photoacoustic Measurement
- Photoacoustic and Photocurrent Studies of Highly Porous TiO_2 Electrodes Sensitized by Quantum-Sized CdS
- 物性評価 SnO2/ZnOナノコンポジット電極の光音響・光電気化学特性
- 22aTN-8 ARPES及びXMCD分光を用いたMnドープBi_2Se_3の電子状態の研究(22aTN 光電子分光(強相関系),領域5(光物性))
- P2-25 ZnS:Mnナノ粒子系の光音響スペクトル(ポスターセッション2,ポスター発表)
- C-4 ナノ構造を有するTiO_2電極の光音響・光電流応答特性(光-超音波エレクトロニクス・非破壊検査,口頭発表)
- Photoacoustic and Photoelectrochemical Current Spectra of Highly Porous, Polycrystalline TiO_2 Films Fabricated with Different Applied Voltage Treatments
- Effect of Voltage Treatment on Modulation Frequency Dependence of the Photoacoustic and Photoelectrochemical Current Spectra of Highly Porous, Polycrystalline TiO_2 Electrodes
- Photoacoustic Studies of Annealed CdS_xSe_ (x=0.26) Nanocrystals in a Glass Matrix
- 光と超音波 PbS量子ドットを吸着したナノ構造TiO電極の光音響・光電気化学特性
- Characterization of Photoexcited Carriers and Thermal Properties of Nanoparticulate TiO2 Film Using Heterodyne Transient Grating Method
- Crystal Growth of CdSe Quantum Dots Adsorbed on Nanoparticle, Inverse Opal, and Nanotube TiO2 Photoelectrodes Characterized by Photoacoustic Spectroscopy
- Characterization of Nanostructured TiO2 Electrodes Sensitized with CdSe Quantum Dots Using Photoacoustic and Photoelectrochemical Current Methods
- Effect of Ligand Carboxylation on Adsorption and Photosensitization in Ru(II)-Complex Dye-Sensitized Nanocrystalline TiO2 Solar Cell
- Optical Absorption, Photoelectrochemical, and Ultrafast Carrier Dynamic Investigations of TiO2 Electrodes Composed of Nanotubes and Nanowires Sensitized with CdSe Quantum Dots
- Photoacoustic and Photoelectrochemical Current Response of Nanostructured TiO2 Electrodes
- Photoacoustic and Photoluminescence Characterization of Passivated and Unpassivated Mn-Doped ZnS Nanoparticles