Organic Solar Cells Based on Ternary Blend Active Layer of Two Donors PTB7, P3HT and Accepter PC61BM
スポンサーリンク
概要
- 論文の詳細を見る
Bulk-heterojunction solar cells were fabricated using ternary blend dichlorobenzene solutions of poly[4,8-bis[(2-ethylhexyl)oxy]benzo[1,2-b:4,5-b']dithiophene-2,6-diyl] [3-fluoro-2-[(2-ethylhexyl)carbonyl]thieno[3,4-b]-thiophenediyl] (PTB7): poly(3- hexylthiophene)(P3HT):[6,6]-phenyl-C61-butyric acid methyl ester (PC61BM) with different weight ratios between PTB7 and P3HT on an indium-tin-oxide-coated glass substrate. The UV-vis absorption spectra of these ternary blend films show that the photon absorptions at the wave lengths of 500 and 700 nm can be adjusted depending on the P3HT polymer weight fraction in the PTB7 and P3HT total weight. The measurement results of the solar cell performance showed that the open circuit voltage Voc continuously increased from 0.62 to 0.79 V as the P3HT fraction increased from 0 to 20 %, while it gradually decreased above 30%. The short circuit current Jsc slightly decreased from 10.4 to 9.0 A/cm2 up to 20%, and it suddenly dropped above 30%. The power conversion efficiency of 4% decreased to 1.8% when the P3HT fraction increased to 30%. These results may suggest that the transports of photo excited electrons and holes between the PTB7 nano domains and P3HT nano domains are disturbed by the differences between the HOMO and LUMO levels of the PTB7 and P3HT.
- The Society of Photopolymer Science and Technology (SPST)の論文
著者
-
Nishioka Yasushiro
Department Of Physics Faculty Of Science University Of Tokyo
-
Fujii Shunjiro
Nanosystem Research Institute National Institute Of Advanced Industrial Science And Technology (aist)
-
Kataura Hiromichi
Nanosystem Research Institute National Institute Of Advanced Industrial Science And Technology (aist)
-
Yanagi Yuichiro
Department of Precision Machinery Engineering, College of Science and Technology, Nihon University
-
Ohori Yurina
Department of Precision Machinery Engineering, College of Science and Technology, Nihon University
-
Hoashi Toshihiro
Department of Precision Machinery Engineering, College of Science and Technology, Nihon University
-
Okukawa Takanori
Department of Precision Machinery Engineering, College of Science and Technology, Nihon University
関連論文
- Fabrication of a Valveless Micropump with Polyimide Membrane
- Effect of 2-Propanol Concentration in Electrolyte Solution on Polypyrrole Actuator Performance
- Lead--Zirconate--Titanate Acoustic Energy Harvesters with Dual Top Electrodes
- Flexible polyimide micropump fabricated using hot embossing (Special issue: Microprocesses and nanotechnology)
- Plastic Flow in bcc ^3He
- Fabrication processes for capacity-equalized mold with fine patterns (Special issue: Microprocesses and nanotechnology)
- Single-Molecule Behaviors of Conjugated 2,2$'$-Bipyridine Derivative Inserted in Matrix Layer Using Dendrimer-Based Template
- Effective Linewidth Measurement of 45-nm-Half-Pitch Ultraviolet Nanoimprint Lithography Patterns by Scanning Electron Microscope Inspection and Extremely Shallow Si Etching (Special Issue : Microprocesses and Nanotechnology)
- Novel Phenylene-Thiophene Oligomer Derivatives with Dibenzothiophene 5,5-Dioxide Core : Synthesis, Characterization, and Applications in Organic Solar Cells
- Improved Performances of Acoustic Energy Harvester Fabricated Using Sol/Gel Lead Zirconate Titanate Thin Film
- Lead-Zirconate-Titanate Acoustic Energy Harvester Equipped with Sound-Collecting Helmholtz Resonator
- Semitransparent Gold-Meshed Electrode Fabricated by Transfer Printing Using Self-Organized Microporous Polymer Mold
- Organic Solar Cells Based on Ternary Blend Active Layer of Two Donors PTB7, P3HT and Accepter PC61BM