Synthesis and Electrochemical Properties of Ramsdellite Type Lithium Titanate Anode Materials by Spray Pyrolysis
スポンサーリンク
概要
- 論文の詳細を見る
Ramsdellite type lithium titanate (Li2Ti3O7) powders were prepared by spray pyrolysis. Chemical and physical properties of Li2Ti3O7 powders were characterized by SEM, DTG, XRD and ICP. As-prepared Li2Ti3O7 precursor powders had a spherical morphology with hollow microstructure, but the irregular shaped morphology was obtained after the calcination above 900 °C. The crystal phase of ramsdellite Li2Ti3O7 was obtained by the calcination at 1100 °C. The first rechargeable capacities of Li2Ti3O7 anode were 168 mAh/g and 82 mAh/g at 0.1 mA/cm2 and 20 mA/cm2, respectively. The retention ratio of discharge capacity was 99 % at 1 mA/cm2 after 100th cycle. The cycle performance of Li2Ti3O7 anode had also high stability at 50 °C.
著者
関連論文
- 酸化マンガン多孔体への含浸処理によるリチウムイオン電池正極材料の合成と電池特性
- 有機酸水溶液の噴霧熱分解法による炭素/チタン酸リチウム粉体の合成と電気化学的特性
- 噴霧熱分解法による球状酸化物フィラーの合成とその性質
- 酸化マンガン多孔体への含浸処理によるリチウムイオン電池正極材料の合成と電池特性
- 鉄道車両用大型高出力マンガン系リチウムイオン電池の開発
- ポリ乳酸/プルロニック系界面活性剤ブレンド材料の特性
- ポリプロピレン/エチレン-ビニルアルコール共重合体芯鞘構造繊維の溶融静電紡糸
- ゾル-ゲル法によるポリブチレンテレフタレート材へのシリカ/ポリメチルメタクリレートハイブリッド薄膜の作製及びその性質
- ゾル-ゲル法による炭素繊維へのアルミナコーティング
- 水熱法により得られた水酸アパタイトナノ結晶のタンパク質吸着特性及び抗菌性
- 水熱合成によるリン酸カルシウムナノ粒子の生成における原料溶液の影響
- アルミナ前駆体を被覆した炭素繊維によるアルミニウム基炭素繊維複合材料の作製及び機械的性質
- リチウムイオン電池用正極材料の開発と噴霧熱分解法により合成した正極材料の特徴 (特集 電気自動車(EV)を支える粉体技術)
- 粉体工学によるリチウムイオン2次電池の高機能化
- テイラー渦を加水分解反応場とする単分散粒子調製法
- 噴霧熱分解法で合成したLiFePO4/C正極材料の電池特性に及ぼす炭素源の影響 (特集 グリーン・プロセッシングによる機能性粉体の合成と応用)
- 噴霧熱分解法によるLiNi_Mn_O_4正極材料の連続合成及び充放電特性
- 噴霧熱分解法で合成したLiFePO_4/C正極材料の電池特性に及ぼす炭素源の影響
- Synthesis and Rechargeable Properties of Na2/3Fe1/3Mn2/3O2 Cathode Active Materials
- Synthesis and Electrochemical Properties of Ramsdellite Type Lithium Titanate Anode Materials by Spray Pyrolysis
- ラムスデライト型チタン酸リチウム負極活物質の合成及び電気化学的特性
- ナトリウムイオン電池用Na_Fe_Mn_O_2正極活物質の合成及び電気化学的特性