酸化マンガン多孔体への含浸処理によるリチウムイオン電池正極材料の合成と電池特性
スポンサーリンク
概要
- 論文の詳細を見る
Spherical porous Mn2O3 powders were prepared by spray pyrolysis. Lithium and aluminum nitrate solution were immersed to porous Mn2O3 powders to obtain LiAlXMn2-XO4 powders. Homogeneous LiAlXMn2-XO4 powders were formed by the calcination at 800°C. SEM observation showed that they had spherical morphology with dense microstructure. XRD revealed that the spinel phase was formed by the calcination at 700°C. LiAlXMn2-XO4 cathode obtained by this method exhibited higher rechargeable capacity and cycle stability than that of LiMn2O4. The rechargeable capacity of LiAl0.05Mn1.95O4 exhibited 120mAh/g at 1C and 90mAh/g at 10C, respectively. 91% of initial discharge capacity was maintained after 500 cycles at a rate of 1C. The doping of aluminum ion was effective for the cycle stability of LiMn2O4 cathode at 50°C.
著者
-
小寺 喬之
福井大学大学院工学研究科ファイバーアメニティエ工学
-
荻原 隆
福井大学大学院工学研究科ファイバーアメニティエ工学
-
山田 基文
福井大学大学院 工学研究科 材料開発工学専攻
-
廣瀬 祥司
福井大学大学院 工学研究科 材料開発工学専攻
-
明神 賢一
福井大学大学院 工学研究科 材料開発工学専攻
関連論文
- 酸化マンガン多孔体への含浸処理によるリチウムイオン電池正極材料の合成と電池特性
- 噴霧熱分解法による球状酸化物フィラーの合成とその性質
- 酸化マンガン多孔体への含浸処理によるリチウムイオン電池正極材料の合成と電池特性
- 鉄道車両用大型高出力マンガン系リチウムイオン電池の開発
- ポリ乳酸/プルロニック系界面活性剤ブレンド材料の特性
- ポリプロピレン/エチレン-ビニルアルコール共重合体芯鞘構造繊維の溶融静電紡糸
- ゾル-ゲル法によるポリブチレンテレフタレート材へのシリカ/ポリメチルメタクリレートハイブリッド薄膜の作製及びその性質
- ゾル-ゲル法による炭素繊維へのアルミナコーティング
- 水熱法により得られた水酸アパタイトナノ結晶のタンパク質吸着特性及び抗菌性
- 水熱合成によるリン酸カルシウムナノ粒子の生成における原料溶液の影響