CO-H2系反応ガスによるダイヤモンドの合成および添加ガス (O2, CO2) の影響について
スポンサーリンク
概要
- 論文の詳細を見る
Diamond was deposited in both film and particle form by microwave plasma CVD from a CO-H2 system at a power input of 220W, an H2 flow of 100cm3/min., and a pressure of 3.3kPa. O2 and CO2 were used as additive gases. In deposition without additives, the rate reached a maximun at 50cm3 CO/min., while idiomorphism was apparent at CO concs<15cm3/min.; for the same CO flow with the O2 additive, the maximum occurred at 1cm3 O2/min. and the idiomorphism appeared at O2 cones>4cm3/min.; and for the same CO flow with CO2, the maximum occurred at 4cm3 CO2/min, and the idiomorphism appeared at CO2 cones>6 cm3/min. The highest deposition rates obtained in this study were 2.8 and 9.2μm/min, for the film and particles, respectively, with a CO-CO2-H2 system. The favorable results make this appear to be the most promising combination for diamond synthesis by microwave CVD.Addition of either O2 or CO2 to this system can form diamond of higher crystallinity comparable to that of naturally occurring type II a.A possible mechanism of deposition from those gases is also suggested.
- 社団法人 表面技術協会の論文
著者
関連論文
- 明道大学における直線翼垂直軸型風力発電システムの実験的研究
- D105 明道大学における直線翼垂直軸型風力発電システムの実験的研究(風車性能1,OS-2 自然エネルギー(1),一般講演,地球温暖化防止と動力エネルギー技術)
- 明道管理学院における直線翼垂直軸型風力発電システムの応用
- 明道大学における直線翼垂直軸型風力発電システムの実験的研究
- チタン合金のM_s点に関する熱力学的考察
- マグネシウム中の水素分析法
- マグネシウム中の水素溶解度
- チタンの水素溶解度におよぼす合金元素の影響
- ベリリウム-チタン2元系合金のベリリウム側平衡状態図
- 水素化金属中の水素定量装置の試作 : 水素化チタン中の水素の定量