濃厚溶液間反応によるバテライト形炭酸カルシウムの生成 (粉体(特集))
スポンサーリンク
概要
- 論文の詳細を見る
Vaterite is generally known as an unstable form of calcium carbonate, but pure vaterite was obtained from the reaction of concentrated aqueous solutions of the CaCl2-Na2CO3 system. Ordinarily in the mechanism of precipitation reaction an important part is played by the degree of concentration of the reactants, whose influence is especially noticeable on the number of the stages. From diluted aqueous solutions of reactants in the CaCl2-Na2CO3 system, it is known that there is only one step of reaction as follows;<BR>CaCl2+Na2CO3→CaCO3(Calcite)+2NaCl<BR>In concentrated reactant a transparent gelatinic membrane appears at the phase boundary of CaCl2 solution (>2N) and Na2CO3 solution (>2N) in the initial stage, which becomes translucent in 15 minutes or more, and the following process of reaction has been observed; CaCl2+Na2CO3→Oriented substance in the initial period at the interface. (a transparent gelatinic membrance)<BR>→CaCO3·mNa2CO3·nH2O<BR>→CaCO3·Na2CO3·n'H2O<BR>→CaCO3 (Vaterite) or CaCO3 (Calcite) at room temperature.<BR>Studies were made of the X-ray diffraction, the infrared absorption spectra, the high-resoltion nuclear magnetic resonance and the electron spin resonance, during the transparent stage and the following stages at the room temperature or 77°K. The result shows that the gelatinic substance is in an amorphous state showing a broad peak at about 15° (θ) by the x-ray diffraction and that CO32-ions are not distributed at random but orient themselves in a definite way, making an angle of 45°-90° with the interface as revealed by the polarized infrared absorption.<BR>The experiment also indicates that the gelatinic substance is viscous in spite of its high water content, and that its watering redient has been restricted by stronger hydrogen-bonds than the original solution. It is interesting to notice the presence of from three to five broad lines of proton magnetic resonance absorption (60Mc) extending from the water level to high magnetic fields.<BR>The E.S.R. signal of gelatinic substance appears at the point of 2.004 (G-Value) at 77°K. It is possible that this points to the presence of H2O-.<BR>This fact suggests that H2O gets strongly polarized in the ionic fields and makes a spur of radical in the gelatinic substance.<BR>The gelatinic substance gradually precipitates by separation of H2O and produces the double salts at room temperature as follows: CaCO3·Na2CO2·nH2O (n≅13), CaCO3·Na2CO3·5H2O (Gaylussite), CaCO3·Na2CO3·2H2O and CaCO3·Na2CO3·H2O (Pirssonite). The major product of the double salts is gaylussite and it is subject to decomposition into vaterite under cectain conditions.<BR>The production of pure vaterite is possible under the following condition.<BR>Original solution; 6N CaCl2-2N Na2CO3, <BR>Reaction temperature; 20-30°C, <BR>Mixing ratio (mol ratio); CaCl2:Na2CO3=1:3, <BR>Reaction time; 30-50min, <BR>The stirrer must be worked slowly (200r/min). When the precipitation is complete the precipitate must be filtered rapidly and washed in the mixture of H2O (70%) -Methanol (30%) and then with ether.
著者
関連論文
- β型半水セッコウの粒子の大きさが高圧DTA曲線に及ぼす影響
- X線回折法による製剤の定量分析(第7報) : 内部標準法による懸濁液剤の定量
- X線回折法による製剤の定量分析(第6報) : 膣錠の定量
- X線回折法による軟膏中の主成分の定量(第4報) : 軟膏中の酢酸ヒドロコルチゾン, クロラムフェニコール, 塩酸テトラサイクリンの定量
- 炭酸ガス法によって生成する水酸化アルミニウムの性状
- X線回折法による軟膏中の主成分の定量(第2報) : 軟膏中の白降汞およびイオウの定量
- X線回折法による軟膏中の主成分の定量(第3報) : 軟膏中のサリチル酸, アミノ安息香酸エチルおよびスルフイソミジンの定量
- X線回折法による軟膏中の主成分の定量(第1報) : 軟膏中のホウ酸と酸化亜鉛の定量
- 水稲体中の重金属類の分布および形態(第2報) : X線マイクロアナライザーによる玄米中の重金属類の形態
- 可溶化コラ-ゲン溶液中でのα-ビス(リン酸)三カルシウムの加水分解に及ぼす反応温度および反応時間の影響
- α-ビス(リン酸)三カルシウムの加水分解に及ぼす可溶化コラ-ゲン濃度の影響^
- 可溶化コラーゲン溶液中で生成したα-ビス(リン酸)三カルシウムの加水分解生成物の熱的性質
- 可溶化コラーゲン溶液中でのα-ビス(リン酸)三カルシウムの加水分解に及ぼす初期pH影響
- 水酸化カルシウムの炭酸化反応
- カルシウム・アルミネート化合物の炭酸化反応
- カルシウム・シリケート化合物の炭酸化反応
- フッ化水素酸(フッ酸)(HF)(酸類, 試薬)
- 硝酸(HNO_3)(酸類, 試薬)
- 硫酸(H_2SO_4)(酸類, 試薬)
- 塩酸(HCl)(酸類, 試薬)
- 界面膜形成に依る水溶液反応の研究
- 分子間化合物に關する研究
- X-ray Diffractometerによる縮合リン酸塩(NaPO3-Na5P3O10系)の定量分析 : X-ray Diffractometerによる工業分析法の研究(IV)
- 濃厚溶液間反応によるバテライト形炭酸カルシウムの生成 (粉体(特集))