Gamma-Ray-Induced Polymerization of Mixed Liposomes Consisting of 2, 4-Octadecadienoyl Groups of Phospholipids and Unpolymerizable Components
スポンサーリンク
概要
- 論文の詳細を見る
We studied the γ-ray-induced polymerization of two mixed-liposome systems containing 1, 2-bis- [(<I>2E, 4E</I>) -octadecadienoyl] -<I>sn</I>-glycero-3-phosphocholine (DODPC) to clarify its mechanism; (a) containing DODPC and 1, 2-dipalmitoyl-<I>sn</I>-glycero-3-phosphocholine (DPPC), or DODPC/DPPC liposome, and (b) containing DODPC, DPPC, Cholesterol (Chol), and stearic acid (SA), or DODPC/DPPC/Chol/SA liposomes was carried out. For each system, various molar ratios of DODPC/DPPC were studied. For DODPC/DPPC/Chol/SA liposomes, the molar ratio of phospholipid/Chol/SA was 7/7/2. Liposomes were prepared by extrusion through a 0.2-μm-pore polycarbonate filter and polymerized by γ-irradiation at a dose rate of 3.3kGy/h at 4°C. Polymerization rate increased when DODPC/DPPC was 5/5 in DODPC/DPPC liposomes and when it was 9/1, 8/2, 7/3, and 5/5 in DODPC/DPPC/Chol/SA liposomes. The degree of polymerization at molar ratio 5/5 for each mixed-liposome system significantly increased compared with that of DODPC liposomes containing no DPPC. For polymerized mixed liposomes stability, mean diameter after one freeze-thaw cycle remained unchanged for molar ratios from 10/0 to 8/2 of either DODPC/DPPC or DODPC/DPPC/Chol/SA liposomes. γ-Ray-induced polymerization of each mixed-liposome system was analyzed using kinetic treatment of polymerization. Although the rate of polymerization for either systems differed from that of DODPC liposomes, the polymerization mechanism was the same. Immiscibility between DODPC and unpolymerizable components was estimated based on the kinetic data of polymerization. Hydrophobic interactions of DPPC and/or Chol with DODPC significantly affected the conformation of DODPC, which rearranges into an easily polymerizable conformation. The rate and degree of polymerization thus increased.
- Japan Oil Chemists' Societyの論文
著者
-
細井 文雄
日本原子力研究所高崎研究所
-
大道 英樹
日本原子力研究所高崎研究所
-
矢野 嘉宏
熊本工業大学工業化学科
-
Yano Yoshihiro
Tsukuba Research Laboratory Nof Corporation
-
中野 善郎
日本油脂株式会社 筑波研究所
-
赤間 和博
日本油脂株式会社筑波研究所
-
徳山 悟
日本油脂株式会社筑波研究所
-
粟井 浩二
日本油脂株式会社 筑波研究所
-
矢野 嘉宏
日本油脂株式会社 筑波研究所
-
大道 英樹
日本原子力研究所 高崎研究所
-
赤間 和博
日本油脂株式会社 筑波研究所
-
徳山 悟
日本油脂株式会社 筑波研究所
-
細井 文雄
日本原子力研究所 高崎研究所
関連論文
- JEM対応真空密閉式蒸着容器を用いたフタロシアニン蒸着薄膜の作製
- 微小重力下における銅フタロシアニン真空蒸着の予備実験 1. 蒸着速度への希ガス圧力の効果
- N-メチロールアクリルアミドの蒸着重合とFT-IRによるその場観察
- 平成13年度日本油化学会エディター賞受賞によせて
- リン脂質に含まれたドコサヘキサエン酸はトリアシルグリセロールに含まれたドコサヘキサエン酸よりも2, 4-ジニトロ-1-フルオロベンセンで惹起された耳介腫脹を強く抑制する
- フタロシアニン-ステアリン酸二源同時蒸着膜とスパッタ銅複合膜の構造解析
- 多孔性セルロ-ス微粒子をマトリックスとした薬物徐放性製剤の調製
- 多孔性微粒子を用いたアスピリン含有カプセルの調製とその薬物徐放性
- 電子線同時グラフト重合による樹脂の水性化 (ポリマ-アロイの分子設計--多成分系高分子の合成と物性)
- ラセミ体エステルの基質の不斉加水分解反応と制御