イオンビームスパッタ法によって作られたボロン薄膜の密度測定
スポンサーリンク
概要
- 論文の詳細を見る
The thickness of amorphous boron films prepared by ion beam sputter deposition is measured using trasmission electron microscopy (TEM). The point of this method is to hold the preparated films at both side with the deposited metal layers of Pt-Pd by vacuum evaporation or W by ion beam sputtering. Especially, metal layer at outside is effective to except the influence of contamination to be polymerzed in TEM.<BR>Based on the ion beam sputter deposition theory, the density of boron films is calculated. As a result, the film density is found to be independent of thickness. The density of amorphous boron films made by ion beam sputter deposition (ρ=2.4±0.18 g/cm<SUP>3</SUP>) is in close agreement with the result obtained by N. N. Greenwood (ρ =2.35 g/cm<SUP>3</SUP>).
- 日本真空協会の論文
著者
関連論文
- 25aTB-2 双晶のないYBCO単結晶の磁化測定
- 高エネルギー重イオン照射による酸化物高温超伝導体の欠陥構造
- 28pYG-6 微粒子中の照射損傷の観察
- 18aTG-10 微粒子中の欠陥集合
- 25pY-7 金微粒子の照射損傷(3)
- ブリスタリングによる応力変調を利用した局所シリコン酸化の観察
- β-FeSi_2 薄膜の結晶構造におけるSi基板処理効果
- イオンビームスパッタリング法による高配向β-FeSi_2の作製
- γ-MnM(M = Fe, Cu, Zn)合金の結晶変態と磁気構造
- 「核融合炉材料の規準」研究会
- 29p-PSB-18 γ-MnRh合金の結晶変態と磁性
- 30a-PS-93 Fe-Niインバー合金のメカニカルアロイングと磁性
- 18pPSB-12 1.5K冷凍機を用いた磁気トルク計の開発
- イオン照射欠陥の"その場"観察
- 透過電子顕微鏡その場観察用二重イオン照射装置
- 25p-H-5 Al中のHeバブルの拡散
- 25p-H-4 Al中のHeバブルの動的挙動のその場観察
- 透過型電子顕微鏡用イオン照射装置(電子顕微鏡内試料イオンビーム処理動的観察記録装置)
- 30p-F-10 アルミニウム中の格子間原子型転位ループ形成における水素の効果
- バブル表面プラズモンの空間分解EELS
- 28p-ZA-14 金微粒子の照射損傷(2)
- 31a-YK-3 金微粒子の照射損傷
- 大電流イオン注入装置によるTiNコーティング
- セラミックス強度材料 炭化珪素(SiC)の照射損傷とEELS分析
- イオンビームスパッタ法によって作られたボロン薄膜の密度測定
- 1. 理工学利用 1. 3 電顕内イオン照射"その場"観察
- 24pPSA-49 1.5K冷凍機を用いた磁気トルク計の開発 II(24pPSA 理論・高温超伝導,領域8(強相関系分野-高温超伝導,強相関f電子系など))