湿式法によるMn<SUB>3</SUB>O<SUB>4</SUB>置換体(MMn<SUB>2</SUB>O<SUB>4</SUB>)の生成反応とイオン分布
スポンサーリンク
概要
- 論文の詳細を見る
A wet method was applied to prepare a spinel type MMn<SUB>2</SUB>O<SUB>4</SUB> (M=Mn, Mg, Zn, Cu, Fe, Co, Ni and Cd) in alkaline water solution below 100°C. When M is Mn, Zn or Co, a stoichiometric spinel is prepared. When M is Mg, Fe or Cd, a partially substituted spinel is obtainable, and chemical compositions of the spinels which have the maximum foreign atom contents are given by Mg<SUB>0.2</SUB>Mn<SUB>2.8</SUB>O<SUB>4</SUB>, Fe<SUB>0.4</SUB>Mn<SUB>2.6</SUB>O<SUB>4</SUB> and Cd<SUB>0.6</SUB>Mn<SUB>2.4</SUB>O<SUB>4</SUB>, respectively. Cu and Ni-substituted spinels are not obtainable by the method. Neutron diffraction measurements show that ZnMn<SUB>2</SUB>O<SUB>4</SUB> and CoMn<SUB>2</SUB>O<SUB>4</SUB> have their ionic distributions of (Zn<SUP>2+</SUP>) [Mn<SUB>2</SUB>]O<SUB>4</SUB> and (Co<SUB>0.84</SUB><SUP>2+</SUP>Mn<SUB>0.16</SUB><SUP>2+</SUP>)[Co<SUB>0.16</SUB><SUP>II+</SUP>Mn<SUB>1.84</SUB><SUP>3+</SUP>]O<SUB>4</SUB>, respectively.
- 社団法人 粉体粉末冶金協会の論文
著者
関連論文
- 層状構造をもつ水和バナジウム酸化物の合成と相転移
- VO_2(A)の相転移と電気的性質(酸化物系導電セラミックス)(導電性セラミックス)
- 9a-D-7 α-Fe_2O_3の微粒子のMossbauer効果
- 層状構造をもつアリカリ含有水和バナジウム酸化物の水熱合成
- 9a-D-8 α-Fe_2O_3の微粒子の形態と磁性
- 5p-G-11 Co_3O_4-Mn_3O_4系固溶体の結晶成長
- α-FeOOH微粒子の磁性 : 磁性(化合物)
- 3a-B-10 α-Fe_2O_3のMorin点の粒度依存性
- 2p-B-13 FeOOHの磁性II
- α-Fe_2O_3微粒子の磁性: 磁性 : 微粒子,薄膜
- 9a-D-6 α.β及びγ-FeOOHの磁性
- 急冷Bi-Sr-Ca-Su-O系の結晶化過程
- Bi-Sr-Ca-Cu-O系超伝導体の部分溶融状態における高温X線測定
- 蓚酸法によるBi系酸化物超伝導体の研究
- 蓚酸塩法によるBi-Pb系超電導体の合成
- 蓚酸塩法によるBi-Pb-Sr-Ca-Cu-O系高温超伝導体の作成
- トンネル構造をもつMnO2多形の結晶構造
- 新化合物"NiMnO2(OH)"の合成と物性
- 熱アルカリ水溶液中のコバルタイト置換体(MCo2O4,M=Cd,Co,Cu,Fe,Mg,Mn,Ni,Zn)の水熱反応
- Mn7+-Mn2+-OH-系の水熱反応
- YBa2Cu3Oxの水による分解挙動に関する研究
- 蓚酸法によるYBa2Cu3O7-xの合成と粉末特性
- アルカリ水溶液中のスピネルフェライトの生成と安定性
- 4番目のMnOOH同質多形(polymorph);δ-MnOOH
- 湿式法によるMn3O4置換体(MMn2O4)の生成反応とイオン分布
- 多層膜における中性子の光学的性質
- 包晶反応によるYBa2Cu3Oxの生成 (酸化物超伝導体)
- Bi,Pb-Sr-Ca-Cu-O系高Tc相の生成と電気特性 (酸化物系超伝導物質と材料) -- (平成元年度春季大会講演特集)