Consolidation of Ultrafine Alumina Powders with SPS Method
スポンサーリンク
概要
- 論文の詳細を見る
SPS consolidation of two ultrafine α-alumina powders (TM-alumina with 100nm and AA-alumina with 230nm) was examined under the two pressurizing conditions of 30MPa and 100MPa. It was found that densification behavior under 30MPa was influenced by the grain size of raw powder alumina and the influence of grain size on the densification was remarkably suppressed under 100MPa. It was also indicated that the grain growth was fairly suppressed in the consolidation of TM-alumina powder even when the powder was consolidated at a higher temperature than 1300°C. Further, the growth of crystallite was suppressed by increasing the applied pressure from 30MPa to 100MPa. Under the condition of 100MPa, nano-structural aluminas with less than 300nm and about 500nm were synthesized by consolidating TM-alumina at 1150°C and AA-alumina at 1200°C, respectively, indicating that SPS method has high capabilities of synthesizing nano-structured ceramics.
- 社団法人粉体粉末冶金協会の論文
著者
-
MAKINO Yukio
Joining & Welding Research Institute, Osaka University
-
SAKAGUCHI MASASHI
Department of Anesthesiology, Gunma University, Graduate School of Medicine
-
Terada Jun
Department of Materials Science & Engineering, Kansai University
-
Akamatsu Katsuya
Department of Materials Science & Engineering, Kansai University
-
Sakaguchi Masashi
Department Of Anesthesiology Gunma University Graduate School Of Medicine
-
Akamatsu Katsuya
Department Of Chemistry And Materials Engineering Faculty Of Chemistry Materials And Bioengineering
-
Terada Jun
Department of Materials Science & Engineering, Kansai University
-
Sakaguchi Masashi
Department of Materials Science & Engineering, Kansai University
関連論文
- Characterization of zirconia (3Y)/SUS410L functionally-graded material fabricated by SPS processing (特集 新成形法,新焼結法と自動車への応用について)
- Low Temperature Millimeter-Wave Sintering of Aluminum Nitride with Oxide Additive of CaO-Al_2O_3-Yb_2O_3 System
- Dense Nano-structured and Preferentially-oriented Anatase Synthesized by Pulsed High Current Heating
- Densification Behavior and Crystallite Growth in Alumina-YSZ Composites Sintered by Millimeter-wave Heating
- OS8(P)-28(OS08W0211) A Study on the Mechanical Properties of Silicon Nitride Ceramics Sintered by 28GHz Millimeter-Wave Heating Method
- Acute thrombus formation in the left atrium after the termination of warfarin
- Estimation of Homogeneity in Pulsed High Current Sintering by Crystallographic Character of Consolidated Anatase
- Consolidation behavior and mechanical properties of SiC with Al2O3 and Yb2O3 consolidated by SPS (特集 電磁プロセスのナノ構造機能材料への応用)
- Influence of Phase Change in Intergranular Oxides to Thermal Conductivity of AIN Sintered by Millimeter-Wave Heating
- Examination of Meek's Model for Microwave Sintering Mechanism (特集 電磁エネルギー焼結)
- Decomposition Rate of Si_3N_4 during Microwave Sintering
- Consolidation of Ultrafine Alumina Powders with SPS Method
- Fabrication of high thermal conductive aluminum/graphitic fiber composites by pulsed electric current sintering (特集 電磁プロセスの新展開)
- Kinetics of Densification and Phase Transformation at Microwave Sintering of Silicon Nitride with Alumina and Yttria or Ytterbia as Additives (特集 放電焼結の基礎と応用)
- Effect of Through Cage on Active Screen Plasma Nitriding Properties
- Application of Millimeter-Wave Heating to Materials Processing(Recent Trends on Microwave and Millimeter Wave Application Technology)
- Application of Band Parameters to Materials Design
- Fabrication of Bulk Ceramics by High-Power Millimeter-Wave Radiation