Hot Hardness of WC-Co/TiC-Al_2O_3 Composite Materials
スポンサーリンク
概要
- 論文の詳細を見る
WC particle was coated with TiC and Al2O3 particles using Co binding one by means of high-speed rotational blending to enhance the degree of mixing. Then the sintered composite material of WC-Co/TiC-Al2O3 was prepared, and the hot hardness was measured up to 800°C to be compared with conventional WC-Co alloy. It was found that the addition of TiC and Al2O3 components in the WC-Co alloy has a strong influence on the hot hardness. The hardness increased with higher amount of TiC from 5 up to 30 by weight percentage, whereas increasing Al2O3 additions reduced the hardness. Particularly, Al2O3 was effective due to its higher chemical stability than TiC at elevated temperature. Then, the highest hardness was obtained with addition of 30TiC-5Al2O3 by weight. This suggests that these materials can further be utilized for high temperature applications.
- 社団法人 化学工学会の論文
- 2002-09-01
著者
-
Kangwantrakool Sukasem
Division Of Material Science And Engineering Graduate School Of Engineering Hokkaido University
-
Shinohara Kunio
Division Of Material Science And Engineering Graduate School Of Engineering Hokkaido University
関連論文
- Quantitative Characterization of Microstructure of WC-Co/TiC-Al_2O_3 Composite Materials with Relate to Mechanical Properties
- New Design of Microstructure of WC-Co/TiC-Al_2O_3 Composite Materials by Mechanical Coating of Particles
- Particle flow model in a spouted bed
- Formation of a sigmoidal release pattern of core particles coated with layers of soluble and permeable particles
- Multiple-Layer Coating of Solids with Impermeable Film Dispersing Permeable Particles for Controlled Release
- Effect of the Porous Structure of a Coating Layer on the Release Rate of Core Particle
- Controlled Release of Core Particle Coated with Soluble Particles in Impermeable Layer
- Mechanical and Thermal Properties of Hot-Pressed Compact of Si_3 N_4 Particles Coated with AIN by CVD
- Estimation of Diameter of Granule Prepared by Spray Drying of Slurry with Fast and Easy Evaporation
- Basic Model of Spray Drying Granulation
- Preparation of large agglomerates of high voidage from charcoal particles for liquid absorption and release
- Agglomerating fluidization of group C particles : major factors of coalescence and breakup of agglomerates
- Density segregation of a binary solids mixture during batch operation in a two-dimensional hopper
- Segregation indices of multi-sized particle mixtures during the filling of a two-dimensional hopper
- Mechanism of particle shape modification by dry impact blending
- Air pressure drop across a particle moving bed in a three-dimensional cold model of a blast furnace
- Comparison of moving bed reactors for chemical vapor deposition coating of fine particles
- Hot Hardness of WC-Co/TiC-Al_2O_3 Composite Materials
- NO Adsorption Characteristics of Agglomerated Zeolite Particles
- Modeling of CVD Coating Inside Agglomerate of Fine Particles
- Size segregation of multicomponent particles during the filling of a hopper
- Preparation of New WC-Co/TiC-Al_2O_3 Composite Materials with Mechanically Coated Particles